Optimized Performances of Thick Film Organic Lighting-Emitting Diodes
WANG Xiu-Ru1, ZHANG Zhi-Qiang2, MA Dong-Ge2, SUN Run-Guang1
1School of Material Science and Engineering, Shanghai University, Jiading Campus, PO Box 815, Shanghai 2018002State Key Laboratory of Polymer Physics and Chemistry, Changchun Institute of Applied Chemistry, Graduate School of the Chinese Academy of Sciences, Chinese Academy of Sciences, Changchun 130022
Optimized Performances of Thick Film Organic Lighting-Emitting Diodes
WANG Xiu-Ru1, ZHANG Zhi-Qiang2, MA Dong-Ge2, SUN Run-Guang1
1School of Material Science and Engineering, Shanghai University, Jiading Campus, PO Box 815, Shanghai 2018002State Key Laboratory of Polymer Physics and Chemistry, Changchun Institute of Applied Chemistry, Graduate School of the Chinese Academy of Sciences, Chinese Academy of Sciences, Changchun 130022
The performance of organic light-emitting diodes (OLEDs) with thick film is optimized. The alternative vanadium oxide (V2O5) and N,N'-di(naphthalene-1-yl)-N,N'-diphenyl-benzidine (NPB) layers are used to enhance holes in the emissive region, and 4,7-dipheny-1,10-phenanthroline (Bphen) doped 8-tris-hydroxyquinoline aluminium (Alq3) is used to enhance electrons in the emissive region, thus ITO/V2O5 (8nm)/NPB (52nm)/V2O5 (8nm)/NPB (52nm)/Alq3 (30 and 45nm)/Alq3:Bphen (30wt%, 30 and 45nm)/LiF (1nm)/Al (120nm) devices are fabricated. The thick-film devices show the turn-on voltage of about 3V and the maximal power efficiency of 4.5lm/W, which is 1.46 times higher than the conventional thin-film OLEDs.
The performance of organic light-emitting diodes (OLEDs) with thick film is optimized. The alternative vanadium oxide (V2O5) and N,N'-di(naphthalene-1-yl)-N,N'-diphenyl-benzidine (NPB) layers are used to enhance holes in the emissive region, and 4,7-dipheny-1,10-phenanthroline (Bphen) doped 8-tris-hydroxyquinoline aluminium (Alq3) is used to enhance electrons in the emissive region, thus ITO/V2O5 (8nm)/NPB (52nm)/V2O5 (8nm)/NPB (52nm)/Alq3 (30 and 45nm)/Alq3:Bphen (30wt%, 30 and 45nm)/LiF (1nm)/Al (120nm) devices are fabricated. The thick-film devices show the turn-on voltage of about 3V and the maximal power efficiency of 4.5lm/W, which is 1.46 times higher than the conventional thin-film OLEDs.
WANG Xiu-Ru;ZHANG Zhi-Qiang;MA Dong-Ge;SUN Run-Guang. Optimized Performances of Thick Film Organic Lighting-Emitting Diodes[J]. 中国物理快报, 2008, 25(12): 4425-4427.
WANG Xiu-Ru, ZHANG Zhi-Qiang, MA Dong-Ge, SUN Run-Guang. Optimized Performances of Thick Film Organic Lighting-Emitting Diodes. Chin. Phys. Lett., 2008, 25(12): 4425-4427.
[1] Walzer K, Maennig B, Pfeiffer M and Leo K 2007 Chem.Rev. 107 1233 [2] Zhu X L, Sun J X, Peng H J, Meng Z G, Wong M and Kwoka H S2005 Appl. Phys. Lett. 87 153508-1 [3] Chen T-H, Liou Y, Wu T J and Chen J Y 2005 Appl.Phys. Lett. 87 243510-1 [4] Reynolds K J, Barker J A, Greenham N C, Friend R H andFrey G L 2002 J. Appl. Phys. 92 7556 [5] Hung L S, Tang C W and Mason M G 1997 Appl. Phys.Lett. 70 152 [6] Huang J S, Li G, Wu E, Xu Q F and Yang Y 2006 Adv.Mater. 18 114 [7] Huang J S, Pfeiffer M, Werner A, Blochwitz J, Leo K andLiu Y S 2002 Appl. Phys. Lett. 80 139 [8] Zhou X, Pfeiffer M, Huang J S, Blochwitz-Nimoth J, Qin DS, Werner A and Drechsel J 2002 Appl. Phys. Lett. 81 922 [9] Matsumoto T, Nakada T, Endo J, Mori K, Kawamura N, Yokoi Aand Kido J 2003 SID 03 DIGEST 27.5L p 979 [10] Wang F X, Qiao X F, Xiong T and Ma D G 2008 Org.Electron. (in press)