摘要The effect of pyrolysis atmosphere is investigated for Bi3.25La0.75Ti3O12 (BLT) films prepared on Pt/TiO2/SiO2/p-Si(100) substrates by sol-gel processes. The pyrolysis is carried out at 400°C for 20min under air or O2 atmosphere and the successive anneal is performed at 700°C for 30min under O2 atmosphere. The pyrolysis under O2 is enough for complete removal of organic species, however after pyrolysis under air, carbon and hydrogen atomic species as organic fragment are partly remained in the film. This incomplete removal of organic fragments affects the grain growth and cause more defects in the film or between interfaces during the annealing for the crystallization of BLT film. The growth direction and grain size of the BLT film is revealed to affect ferroelectric properties. The remanent polarization Pr for the BLT films of pyrolysis in O2 and air are measured to be 18.85μC/cm2 and 12.56μC/cm2, respectively. The defects degrade the fatigue property dramatically for the film of pyrolysis in air. It can be concluded that the pyrolysis is an important procedure to control ferroelectric properties.
Abstract：The effect of pyrolysis atmosphere is investigated for Bi3.25La0.75Ti3O12 (BLT) films prepared on Pt/TiO2/SiO2/p-Si(100) substrates by sol-gel processes. The pyrolysis is carried out at 400°C for 20min under air or O2 atmosphere and the successive anneal is performed at 700°C for 30min under O2 atmosphere. The pyrolysis under O2 is enough for complete removal of organic species, however after pyrolysis under air, carbon and hydrogen atomic species as organic fragment are partly remained in the film. This incomplete removal of organic fragments affects the grain growth and cause more defects in the film or between interfaces during the annealing for the crystallization of BLT film. The growth direction and grain size of the BLT film is revealed to affect ferroelectric properties. The remanent polarization Pr for the BLT films of pyrolysis in O2 and air are measured to be 18.85μC/cm2 and 12.56μC/cm2, respectively. The defects degrade the fatigue property dramatically for the film of pyrolysis in air. It can be concluded that the pyrolysis is an important procedure to control ferroelectric properties.
(Dielectric, piezoelectric, ferroelectric, and antiferroelectric materials)
引用本文:
LI Jian-Jun;YU Jun;WU Yun-Yi;LI Jia;WANG Yun-Bo;ZHOU Wen-Li. Effect of Pyrolysis Atmosphere on Ferroelectric Properties of Bi3.25La0.75Ti3O12 Films Prepared by Sol-Gel Method[J]. 中国物理快报, 2009, 26(3): 37702-037702.
LI Jian-Jun, YU Jun, WU Yun-Yi, LI Jia, WANG Yun-Bo, ZHOU Wen-Li. Effect of Pyrolysis Atmosphere on Ferroelectric Properties of Bi3.25La0.75Ti3O12 Films Prepared by Sol-Gel Method. Chin. Phys. Lett., 2009, 26(3): 37702-037702.
[1] Scott J F and Araujo C A 1989 Science 246 1400 [2] Shannigrahi S R and Jang H M 2001 Appl. Phys. Lett. 79 1051 [3] Chon U, Yi G C and Jang H M 2001 Appl. Phys. Lett. 78 658 [4] Kingon A 1999 Nature 401 658 [5] Wang Y, Wong K H and Wu W B 2002 Chin. Phys. Lett. 19 566 [6] Chen H D, Udayakumar K R, Gaskey C J and Cross L E 1995 Appl. Phys. Lett. 67 3411 [7] Nakamura T, Nakao Y, Kamisawa A and Takasu H 1994 Appl. Phys. Lett. 65 1522 [8] Park B H, Kang B S, Bu S D, Noh T W, Lee J and Jo W 1999 Nature 401 682 [9] Yan Z, Zhang W T, Wang Y, Zhang X, Li L, Zhao Q X, Du Jand Liu B T 2007 Chin. Phys. Lett. 24 3559 [10] Li W, Ma J, Song C H, Bao P, Lu X M, Zhu J S and Wang Y N2004 Chin. Phys. Lett. 21 544 [11] Lotgering F K 1959 J. Inorg. Nucl. Chem. 9113 [12] Lu C J, Qiao Y, Qi Y J, Chen X Q and Zhu J S 2005 Appl. Phys. Lett. 87 222901 [13] Sun C L, Chen S Y, Chen S B and Chin A 2002 Appl.Phys. Lett. 80 1984 [14] Kim K T, Kim C I, Kang D H and Shim I W 2002 J. Mod.Phys. B 16 4469 [15] Takenaka T and Sakata K 1980 Jpn. J. Appl. Phys. 19 31 [16] Ramesh R, Luther K, Wilkens B, Hart D L, Wang E, TrasconJ M, Inam A, Wu X D and Venkatesan T 1990 Appl. Phys. Lett. 57 1505 [17] Yau C Y, Palan R, Tran K and Buchanan R C 2005 Appl.Phys. Lett. 86 032907 [18] Haertling G H 1999 J. Am. Ceram. Soc. 82 797
2009, Vol. 26 