摘要Low-density materials, commercially available hydrogensilsesquioxane (HSQ) offer a low dielectric constant. HSQ films can be obtained by spin on deposition (SOD). In this work, low-dielectric-constant HSQ films are prepared by using D5 (decamethylcyclopentasiloxane) as sacrificial porous materials. The dielectric constant of silica films significantly changes from 3.0 to 2.4. We report the structural aspects of the films in relation to their composition after annealed at 300°C, 400°C, and 500°C for 1.5h in nitrogen ambient and annealed at 400°C for 1.5h in vacuum. Si--OH appears after annealed at 400°C for 1.5h in vacuum. The results indicate that the proper condition is in nitrogen ambient. Intensity of the Si--H peak increases with the increasing temperature. Fourier transform infrared spectroscopy is used to identify the network structure and cage structure of Si--O--Si bonds and other possible bonds. Dielectric constant k is significantly lowered by annealing at 350°C for 1.5h in nitrogen ambient. The I--V and C--V measurements are used to determine the dielectric constant, the electric resistivity and the breakdown electric field.
Abstract：Low-density materials, commercially available hydrogensilsesquioxane (HSQ) offer a low dielectric constant. HSQ films can be obtained by spin on deposition (SOD). In this work, low-dielectric-constant HSQ films are prepared by using D5 (decamethylcyclopentasiloxane) as sacrificial porous materials. The dielectric constant of silica films significantly changes from 3.0 to 2.4. We report the structural aspects of the films in relation to their composition after annealed at 300°C, 400°C, and 500°C for 1.5h in nitrogen ambient and annealed at 400°C for 1.5h in vacuum. Si--OH appears after annealed at 400°C for 1.5h in vacuum. The results indicate that the proper condition is in nitrogen ambient. Intensity of the Si--H peak increases with the increasing temperature. Fourier transform infrared spectroscopy is used to identify the network structure and cage structure of Si--O--Si bonds and other possible bonds. Dielectric constant k is significantly lowered by annealing at 350°C for 1.5h in nitrogen ambient. The I--V and C--V measurements are used to determine the dielectric constant, the electric resistivity and the breakdown electric field.
YIN Gui-Qin;NING Zhao-Yuan;YUAN Qiang-Hua. Structure Characterization of HSQ Films for Low Dielectrics Using D5 as Sacrificial Porous Materials[J]. 中国物理快报, 2007, 24(12): 3532-3534.
YIN Gui-Qin, NING Zhao-Yuan, YUAN Qiang-Hua. Structure Characterization of HSQ Films for Low Dielectrics Using D5 as Sacrificial Porous Materials. Chin. Phys. Lett., 2007, 24(12): 3532-3534.
[1] Seidel T E and Ting C H 1995 Mater. Res. Soc. Symp.Proc. 381 3 [2] Pai P L and Ting C H 1989 Proc. IEEE VIMC Conference(Santo Clara 16--18 June 1989) p 258 [3] 1997 The Semiconductor Technology Roadmap forSemiconductors (San Jose, CA: Semiconductor Industry Association) [4] Liu P T, Chang T C, Hsu K C, Tseng T Y, Chen L M, Wang C Jand Sze S M 2002 Thin Solid Films 414 1 [5] Gill A 2001 Diam. Relat. Mater 10 234 [6] Maex K, Baklanov M R, Shamiryan D, Iacopi F, Brongersma SH and Yanovitskaya Z S 2003 J. Appl. Phys. 93 8793 [7] Liu P T, Chang T C, Yang Y L, Cheng Y F and Sze S M 2000 IEEE Trans. Electron. Devices 47 1733 [8] Liu P T, Chang T C, Su H, Mor Y S, Yang Y and Chung H, HouJ and Sze S M 2001 J. Electrochem. Soc. 148 F30
2007, Vol. 24 