Abstract:Continuous solidification experiments are carried out with Al-Pb alloys under the effect of a direct current. The microstructure evolution in the samples is calculated. The numerical results obtained indicate that a direct current has great effects on the solidification of immiscible alloys. It mainly affects the microstructure evolution during a liquid-liquid decomposition by changing the spatial motions of the minority phase droplets and the temperature field in front of the solidification interface. A sample with either a well dispersed or a core/shell microstructure can be obtained by solidifying Al-Pb alloys under the effect of properly selected direct currents.
. [J]. 中国物理快报, 2012, 29(8): 88104-088104.
JIANG Hong-Xiang, and ZHAO Jiu-Zhou. Effect Mechanism of a Direct Current on the Solidification of Immiscible Alloys. Chin. Phys. Lett., 2012, 29(8): 88104-088104.
[1] Zhang X M, Wang W L, Ruan Y and Wei B B 2010 Chin. Phys. Lett.27 026401 [2] Li Z Q, Wang W L, Zhai W and Wei B B 2011 Acta Phys. Sin.60 108101 (in Chinese) [3] Carlberg T and Fredriksson H 1980 Metall. Trans. A 11 1665 [4] Walter H U 1984 Proc. Workshop Effect Gravity Solidification Immiscible Alloys (Stockholm) p 47 [5] Potard C 1982 Acta Astronaut.9 245 [6] Lohberg K and Dietl V 1978 NASA TM-78125 p VIII-1 [7] Fujii H, Kimura T, Kitaguchi H, Kumakura H, Togano K and Mohri M 1995 J. Mater. Sci.30 3429 [8] Zhang L, Wang E G, Zuo X W and He J C 2008 Acta Metall. Sin.44 165 (in Chinese) [9] Yasuda H, Ohnaka I, Fujimoto S, Takezawa N, Tsuchiyama A, Nakano T and Uesugi K 2006 Scr. Mater.54 527 [10] Zhang Y K, Gao J, Nagamatsu D, Fukuda T, Yasuda H, Kolbe M and He J C 2008 Scr. Mater.59 1002 [11] Wang J, Zhong Y B, Ren W L, Lei Z S, Ren Z M and Xu K D 2009 Acta Phys. Sin.58 893 (in Chinese) [12] Yasuda H, Ohnaka I, Kawakami O, Ueno K and Kishio K 2003 ISIJ Int.43 942 [13] Wang J, Zhong Y B, Wang C, Wang Z Q, Ren Z M and Xu K D 2011 Acta Phys. Sin.60 076101 (in Chinese) [14] Chen F and Shu G J 1998 J. Mater. Sci. Lett.17 259 [15] Li H L and Zhao J Z 2008 Appl. Phys. Lett.92 241902 [16] He J, Zhao J Z and Ratke L 2006 Acta Mater.54 1749 [17] Zhao J Z and Ratke L 2004 Scr. Mater.50 543 [18] Qin R S and Zhou B L 1998 Int. J. Non-Equilib. Process.11 77 [19] Yu S K, Sommer F and Predel B 1996 Z. Metallkd.87 574 [20] Merkwitz M, Weise J, Thriener K and Hoyer W 1998 Z. Metallkd.89 247 [21] Thompson C V and Spaepen F 1983 Acta Metall.31 2021 [22] Beer S Z 1972 Liq. Met. (New York: Marcel Dekker Inc.) p 431 [23] Li H L, Zhao J Z, Zhang Q X and He J 2008 Metall. Mater. Trans. A 39 3308 [24] Takaimchi I and Roderick I L G 2006 Physical Properties Liquid Metals translated by Xian A P and Wang L W (Beijing: Science Press) p 255