摘要By changing the initial elements, we obtain high-quality samples of Al-Cu-Co decagonal quasicrystals with a wide range of composition. The sizes of the samples are typically several centimetres in length and 2-3mm in diameter. These samples are identified to be decagonal single grains by powder x-ray diffraction method, and the composition is homogeneous confirmed by EDX and chemical method.
Abstract:By changing the initial elements, we obtain high-quality samples of Al-Cu-Co decagonal quasicrystals with a wide range of composition. The sizes of the samples are typically several centimetres in length and 2-3mm in diameter. These samples are identified to be decagonal single grains by powder x-ray diffraction method, and the composition is homogeneous confirmed by EDX and chemical method.
[1] Tsai A P, Inoue A and MhsumotoT 1989 Mater. Trans.JIM 30 463 [2] Shechtman D, Blech I, Gratius D and Cahn J M 1984 Phys. Rev. Lett. 53 1951 [3] Gille G, Dreier P, Gr\"{aber M and Scholpp T 1999 J.Crystal Growth 207 95 [4]Yokoyama Y, Note R, Yamaguchi A, Inoue A, Fukaura K andSunada H 1999 Mater. Trans. JIM 40 23 [5] Fisher I R et al 1999 Philos. Mag. B 79 425 [6] Yokoyama Y, Note R and Kimuya S 1997 Mater. Trans.JIM 38 943 [7] Sato T J, Hirano T and Tsai A P 1998 J. Cryst.Growth 191 545 [8] He L X, Wu Y K and Kuo K H 1988 J. Mater. Sci 7 1284 [9].Fisher I R, Islam Z, Danchula A F, Cheon K O, Kramer M J,Canfield P C and Goldman A I 1998 Philos. Mag. B 77 1601 [10]Yokoyama Y and Etal Y 1999 Mater. Trans. JIM 40 123 [11]Wang Y P, Zhang D L and Chen L F 1993 Phys. Rev. B 48 1054.