Creep Behaviour of Fe--Mn Binary Alloys
O. Sahin, N. Ucar
Department of Physics, Art and Science Faculty, Suleyman Demirel University, Isparta, Turkey
Creep Behaviour of Fe--Mn Binary Alloys
O. Sahin;N. Ucar
Department of Physics, Art and Science Faculty, Suleyman Demirel University, Isparta, Turkey
关键词 :
61.66.Dk ,
61.72.Hh ,
62.20.x ,
62.20.Hg
Abstract : Tensile creep behaviour of fine-grained Fe--Mn binary alloys containing 0.42--1.21wt.% Mn has been investigated in the temperature range from room temperature to 475K under 10--50MPa. Tensile tests are carried out with a constant cross-head speed under uniaxial load at a strain rate 10-4 s-1 . Stress exponent and activation energy are determined to clarify deformation mechanism. The obtained variation of steady state creep rate with respect to the applied stress for Fe--Mn binary alloys exhibits two distinct regimes at about 20MPa, indicating a possible change in creep mechanism. The average stress exponent is approximately 2.2, which is a characteristic of grain boundary sliding in the alloys. The activation energy for plastic flow varies from 135 to 92kJ/mol, depending on the Mn content.
Key words :
61.66.Dk
61.72.Hh
62.20.x
62.20.Hg
出版日期: 2006-11-01
:
61.66.Dk
(Alloys )
61.72.Hh
(Indirect evidence of dislocations and other defects (resistivity, slip, creep, strains, internal friction, EPR, NMR, etc.))
62.20.x
62.20.Hg
(Creep)
[1]
HOU Ting-Ping;WANG Ren-Hui;GUI Jia-Nian;WANG Jian-Bo;ZHAO Dong-Shan;GUO Jun-Qing. Experimental Observation on Orientation Relationship between Binary Cd5.7 Yb Quasicrystal and its Crystalline Approximant Cd6 Yb [J]. 中国物理快报, 2006, 23(5): 1253-1256.
[2]
SONG Zhen-Fei;ZHU Wen-Jun;DENG Xiao-Liang;HE Hong-Liang. Crystal-Orientation Dependent Evolution of Edge Dislocations from a Void in Single Crystal Cu [J]. 中国物理快报, 2006, 23(11): 3041-3044.
[3]
Emad A. Badawi. Migration Enthalpy of Thermal Vacancies by Positron Spectroscopy [J]. 中国物理快报, 2005, 22(8): 1998-2001.
[4]
XIA Ji-Lin;LIU Bo;SONG Zhi-Tang;FENG Song-Lin;CHEN Bomy. Electrical Properties of Ag-Doped Ge2 Sb2 Te5 Films Used for Phase Change Random Access Memory [J]. 中国物理快报, 2005, 22(4): 934-937.
[5]
XU Cheng;LIU Bo;SONG Zhi-Tang;FENG Song-Lin;CHEN Bomy. Characteristics of Sn-Doped Ge2 Sb2 Te5 Films Used for Phase-Change Memory [J]. 中国物理快报, 2005, 22(11): 2929-2932.
[6]
AN Zheng-Hua;ZHANG Miao;MEN Chuan-Ling;SHEN Qin-Wo;LIN Zi-Xin;LI Kai-Cheng;LIN Cheng-Lu. Behaviour of Oxygen-Implanted and Hydrogen-Implanted SiGe/Si Heterostructure [J]. 中国物理快报, 2002, 19(3): 413-415.
[7]
YIN Long-Wei;LI Mu-Sen;YUAN Quan;XU Bin;HAO Zhao-Yin. Characterization of Growth Hillocks on the Surface of High-Pressure Synthetic Diamonds [J]. 中国物理快报, 2002, 19(11): 1707-1710.
[8]
RUAN Yong-Feng;Hiroshi NAKAO;Takatomo SASAKI. BO2 -F+ Centers in the Radiation-damaged YCOB Crystals [J]. 中国物理快报, 2000, 17(12): 896-898.
[9]
LIU Chang-Song;ZHU Zhen-Gang;XIA Jun-Chao;SUN De-Yan. Different Cooling Rate Dependences of Different Microstructure Units in Aluminium Glass by Molecular Dynamics Simulation
[J]. 中国物理快报, 2000, 17(1): 34-36.
[10]
HAN Fu-sheng;ZHU Zhen-gang;WANG Shan-ying;LIU Chang-song. Nonlinear Internal Friction Character of Foamed Aluminum [J]. 中国物理快报, 1998, 15(1): 52-53.
[11]
LI Fang-hua;CHENG Yi-fan. Relationship Between Octagonal Quasicrystal and β-Mn Type Crystal in Cut Description [J]. 中国物理快报, 1996, 13(3): 199-202.