摘要The influence of γ' precipitate on the acoustic nonlinearity is investigated for a nickel-based superalloy, which is subjected to creep deformation. During creep deformation, the cuboidal γ' precipitate is preferentially coarsened in a direction perpendicular to the applied stress axis. The length and shape factor of the γ' precipitate increase with creep time. The increase of relative acoustic nonlinearity with increasing fraction of creep life is discussed in relation to the rafting of γ' precipitate, which is closely related to the scattering and distortion of the acoustic wave.
Abstract:The influence of γ' precipitate on the acoustic nonlinearity is investigated for a nickel-based superalloy, which is subjected to creep deformation. During creep deformation, the cuboidal γ' precipitate is preferentially coarsened in a direction perpendicular to the applied stress axis. The length and shape factor of the γ' precipitate increase with creep time. The increase of relative acoustic nonlinearity with increasing fraction of creep life is discussed in relation to the rafting of γ' precipitate, which is closely related to the scattering and distortion of the acoustic wave.
Chung-Seok KIM;Cliff J. LISSENDEN. Precipitate Contribution to the Acoustic Nonlinearity in Nickel-Based Superalloy[J]. 中国物理快报, 2009, 26(8): 86107-086107.
Chung-Seok KIM, Cliff J. LISSENDEN. Precipitate Contribution to the Acoustic Nonlinearity in Nickel-Based Superalloy. Chin. Phys. Lett., 2009, 26(8): 86107-086107.
[1] Li J and Wahi R H 1995 Acta Metall. Mater. 43507 [2] Miura H, Akahoshi K and Suzuki K 2009 NDT {\& EInt. 42 188 [3] V\'{eron M, Br\'{echet Y and Louchet F 1996 ActaMater. 44 3633 [4] Kim C S, Kwun S I and Park I K 2008 J. Nucl. Mater. 377 496 [5] Cantrell J H and Yost W T 2000 Appl. Phys. Lett. 77 1952 [6] Kim C S and Park I K 2008 J. Nucl. Sci. Tech. 45 1036 [7] Kim C S, Park I K and Jhang K Y 2009 NDT {\& E Int. 42 204 [8] Deng M and Pei J 2007 Appl. Phys. Lett. 90121902 [9] Kim C S, Kim Y H and Kim I H 2005 Key Eng. Mater. 297--300 2134 [10] Jhang K 2000 IEEE Trans. Ultrason. Ferroelectr.Freq. Control 47 540 [11] Hikata A, Chick B B and Elbaum C 1965 J. Appl.Phys. 36 229 [12] Ledbetter H M, Fields R J and Datta S K 1987 ActaMetall. 35 2393 [13] Vivekanandan R and Kutty T R N 1989 Powder Tech. 57 181