One-on-One and R-on-One Tests on KDP and DKDP Crystals with Different Orientations
HU Guo-Hang1,2, ZHAO Yuan-An1, SUN Shao-Tao3, LI Da-Wei1, SUN Xun3, SHAO Jian-Da1, FAN Zheng-Xiu1
1Key Laboratory of Material Science and Technology for High Power Lasers, Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Sciences, Shanghai 2018002Graduate School of Chinese Academy of Sciences, Beijing 1000493State Key Laboratory of Crystal Materials, Shandong University, Jinan 250100
One-on-One and R-on-One Tests on KDP and DKDP Crystals with Different Orientations
HU Guo-Hang1,2, ZHAO Yuan-An1, SUN Shao-Tao3, LI Da-Wei1, SUN Xun3, SHAO Jian-Da1, FAN Zheng-Xiu1
1Key Laboratory of Material Science and Technology for High Power Lasers, Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Sciences, Shanghai 2018002Graduate School of Chinese Academy of Sciences, Beijing 1000493State Key Laboratory of Crystal Materials, Shandong University, Jinan 250100
摘要By testing a substantial number of tripler and z-cut KDP and DKDP crystals, we have observed that at 355nm, the laser induced damage threshold in the R-on-one test is higher than that in the one-on-one test. It is proved that laser conditioning is an efficient way to improve the damage resistance. The efficiency of laser conditioning becomes increasingly good with smaller ramping fluence steps. We have also found that the damage resistance of the z-cut crystal is higher than the tripler cut, and the pinpoint number is definitely less in the z-cut crystal. The reason for these observations is discussed.
Abstract:By testing a substantial number of tripler and z-cut KDP and DKDP crystals, we have observed that at 355nm, the laser induced damage threshold in the R-on-one test is higher than that in the one-on-one test. It is proved that laser conditioning is an efficient way to improve the damage resistance. The efficiency of laser conditioning becomes increasingly good with smaller ramping fluence steps. We have also found that the damage resistance of the z-cut crystal is higher than the tripler cut, and the pinpoint number is definitely less in the z-cut crystal. The reason for these observations is discussed.
(Optical properties of bulk materials and thin films)
引用本文:
HU Guo-Hang;ZHAO Yuan-An;SUN Shao-Tao;LI Da-Wei;SUN Xun;SHAO Jian-Da;FAN Zheng-Xiu. One-on-One and R-on-One Tests on KDP and DKDP Crystals with Different Orientations[J]. 中国物理快报, 2009, 26(8): 87801-087801.
HU Guo-Hang, ZHAO Yuan-An, SUN Shao-Tao, LI Da-Wei, SUN Xun, SHAO Jian-Da, FAN Zheng-Xiu. One-on-One and R-on-One Tests on KDP and DKDP Crystals with Different Orientations. Chin. Phys. Lett., 2009, 26(8): 87801-087801.
[1] De Yoreo J, Burnham A and Whitman P 2002 Int. Mater.Rev. 47 113 [2] Burnham A, Hackel L, Wegner P, Parham T, Hrubesh L,Penetrante B, Whitman P, Demos S, Menapace J, Runkel M, Fluss M,Feit M, Key M and Biesiada T 2002 Proc. SPIE 4679 173 [3] Burnham A, Runkel M, Feit M, Rubenchik A, Folyd R, Land T,Siekhaus W and Hawley-Fedder R 2003 Appl. Opt. 42 5483 [4] Hu G H, Zhao Y A, Sun S T, Li D W, Sun X, Shao J D and FanZ X 2009 Chin. Phys. Lett. 26 097802 Hu G H, Zhao Y A, Sun S T, Li D W, Sun X, Shao J D and Fan ZX 2009 Chin. Phys. Lett. 26 097803 [5] Feit M and Rubenchik A 2004 Proc. SPIE 5273 74 [6] Adams J, Jarboe J, Carr C, Feit M, Hackel R, Halpin J,Honig J, Lane L, Luthi R, Peterson J, Ravizza D, Ravizza F,Rubenchik A, Sell W, Vickers J, Weiland T, Wennberg T, Willard D andYeoman M 2007 Proc. SPIE 6403 64031M-1 [7] DeMange P, Negres R, Carr C, Radousky H and Demos S 2005 Proc. SPIE 5991 599107-1 [8] Runkel M and Burnham A 2001 Proc. SPIE 4347408 [9] Carr C, Feit M and Rubenchik A 2005 Proc. SPIE 5991 59911Q-1