Blue-Green Light Emission from a-SiCx :H-Based Fabry--Perot Microcavities
YUE Rui-Feng, YAO Yong-Zhao, LIU Li-Tian
Institute of Microelectronics, Tsinghua University, Beijing 100084
Blue-Green Light Emission from a-SiCx :H-Based Fabry--Perot Microcavities
YUE Rui-Feng;YAO Yong-Zhao;LIU Li-Tian
Institute of Microelectronics, Tsinghua University, Beijing 100084
关键词 :
78.60.Fi ,
81.15.Gh ,
85.60.Jb
Abstract : A Si-based novel Fabry--Perot microcavity device that can emit blue-green light at room temperature is proposed and fabricated. One of its Bragg reflectors consists of periodically stacked a-SiO2 /a-Si:H layers deposited on the glass by plasma enhanced chemical vapour deposition. The other reflector is a sputtered Al film. The active region between both the reflectors is constructed by a p-type a-SiCx :H/intrinsic-type a-SiCx :H junction from which the electroluminescence (EL) is originated. The EL spectra of this device are recorded by RENISHAW RM2000, a sharp and strong EL peak at 483nm with FWHM of 20nm is observed when the device is driven by dc voltages of 8V, 12V and 18V at room temperature. The intensity of EL increases with the applied voltage while the luminescence wavelength keeps unchanged. Compared with the EL spectra from the sample without the Bragg reflector, the luminescence intensity is about 10 times enhanced and the peak is narrowed greatly. The luminescence mechanism is analysed in detail.
Key words :
78.60.Fi
81.15.Gh
85.60.Jb
出版日期: 2006-02-01
:
78.60.Fi
(Electroluminescence)
81.15.Gh
(Chemical vapor deposition (including plasma-enhanced CVD, MOCVD, ALD, etc.))
85.60.Jb
(Light-emitting devices)
引用本文:
YUE Rui-Feng;YAO Yong-Zhao;LIU Li-Tian. Blue-Green Light Emission from a-SiCx :H-Based Fabry--Perot Microcavities[J]. 中国物理快报, 2006, 23(2): 482-485.
YUE Rui-Feng, YAO Yong-Zhao, LIU Li-Tian. Blue-Green Light Emission from a-SiCx :H-Based Fabry--Perot Microcavities. Chin. Phys. Lett., 2006, 23(2): 482-485.
链接本文:
https://cpl.iphy.ac.cn/CN/
或
https://cpl.iphy.ac.cn/CN/Y2006/V23/I2/482
[1]
YONG Zhen-Zhong;GONG Jin-Long;WANG Zhen-Xia;ZHU Zhi-Yuan;HU Jian-Gang;PAN Qiang-Yan. Field Emission Enhancement of Carbon Nanotubes by Surface Modification [J]. 中国物理快报, 2007, 24(1): 233-235.
[2]
LI Meng-Ke;WANG De-Zhen;SHI Feng;DING Sheng;JIN Hong. Growth and Characterization of Trumpet-Shaped ZnO Microtube Arrays on Si Substrates [J]. 中国物理快报, 2007, 24(1): 236-239.
[3]
ZHU Yan-Xu;XU Chen;HAN Jun;SHEN Guang-Di. Flip-Chip GaN-Based Light-Emitting Diodes with Mesh-Contact Electrodes [J]. 中国物理快报, 2007, 24(1): 268-270.
[4]
CHEN Hong-Da;LIU Hai-Jun;LIU Jin-Bin;GU Ming;HUANG Bei-Ju. Silicon Light Emitting Devices in CMOS Technology [J]. 中国物理快报, 2007, 24(1): 265-267.
[5]
WU Nan-Chun;XIA Yi-Ben;TAN Shou-Hong;WANG Lin-Jun;LIU Jian-Min;SU Qing-Feng. Influence of Positive Bias on Electrical Properties of Undoped Nanocrystalline Diamond Films [J]. 中国物理快报, 2006, 23(9): 2595-2597.
[6]
CAO Yu-Lian;LIAN Peng;MA Wen-Quan;WANG Qing;WU Xu-Ming;HE Guo- Rong;LI Hui;WANG Xiao-Dong;SONG Guo-Feng;CHEN Liang-Hui. Influence of GaAsP Insertion Layers on Performance of InGaAsP/InGaP/AlGaAs Quantum-Well Laser [J]. 中国物理快报, 2006, 23(9): 2586-2586.
[7]
WANG Jian-Feng;ZHANG Bao-Shun;ZHANG Ji-Cai;ZHU Jian-Jun;WANG Yu-Tian;CHEN Jun; LIU Wei;JIANG De-Sheng;YAO Duan-Zheng; YANG Hui. Reduction of Dislocations in GaN Epilayer Grown on Si (111) Substrates using a GaN Intermedial Layer [J]. 中国物理快报, 2006, 23(9): 2591-2594.
[8]
YU Nai-Sen;GUO Li-Wei;CHEN Hong;XING Zhi-Gang;WANG Jing;ZHU Xue-Liang;PENG Ming-Zeng;YAN Jian-Feng;JIA Hai-Qiang;ZHOU Jun-Ming. Luminescent Characteristics of Near Ultraviolet InGaN/GaN MQWs Grown on Grooved Sapphire Substrates Fabricated by Wet Chemical Etching [J]. 中国物理快报, 2006, 23(8): 2243-2246.
[9]
WANG Bao-Zhu;WANG Xiao-Liang;HU Guo-Xin;RAN Jun-Xue;WANG Xin-Hua;GUO Lun-Chun;XIAO Hong-Ling;LI Jian-Ping;ZENG Yi-Ping;LI Jin-Min;WANG Zhan-Guo. Growth and Annealing Study of Mg-Doped AlGaN and GaN/AlGaN Superlattices [J]. 中国物理快报, 2006, 23(8): 2187-2189.
[10]
LU Hong-Liang;LI Yan-Bo;XU Min;DING Shi-Jin;SUN Liang;ZHANG Wei;WANG Li-Kang. Characterization of Al2 O3 Thin Films on GaAs Substrate Grown by Atomic Layer Deposition [J]. 中国物理快报, 2006, 23(7): 1929-1931.
[11]
FENG Xue-Yuan;ZHANG Jia-Yu;XU Chun-Xiang;QIAO Yi;CUI Yi-Ping. Electroluminescence of a Multi-Layered Organic Light-Emitting Diode Utilizing Trans-4-[p-[N-methyl-N-(hydroxymethyl)amino]styryl]-N-Methylphridinium Tetraphenylborate as the Active Layer [J]. 中国物理快报, 2006, 23(6): 1607-1609.
[12]
ZHOU Bing-Qing;LIU Feng-Zhen;ZHANG Qun-Fang;XU Ying;ZHOU Yu-Qin;LIU Jin-Long;ZHU Mei-Fang. Fabrication of c-Si:H(p)/c-Si(n) Heterojunction Solar Cells with Microcrystalline Emitters [J]. 中国物理快报, 2006, 23(6): 1638-1640.
[13]
SUN Jian;BAI Yi-Zhen;YANG Tian-Peng;XU Yi-Bin;WANG Xin-Sheng;DU Guo-Tong;WU Han-Hua. Deposition of ZnO Films on Freestanding CVD Thick Diamond Films [J]. 中国物理快报, 2006, 23(5): 1321-1323.
[14]
ZHANG Hong-Mei;YOU Han;SHI Jia-Wei;GUO Shu-Xu;WANG Wei;LIU Ming-Da;MA Dong-Ge. High Efficiency Red Organic Light-Emitting Diodes Based on Microcavity Structure [J]. 中国物理快报, 2006, 23(5): 1335-1338.
[15]
WANG Xiao-Ping;WANG Li-Jun;ZHANG Bing-Lin;YAO Ning;ZANG Qi-Ren;CHEN Jun;DUAN Xin-Chao. An Effective Method for Improvement of Field Electron Emission Site Density and Uniformity of Amorphous Carbon Thin Films [J]. 中国物理快报, 2006, 23(5): 1314-1316.