Thermal Stability and Spectroscopic Properties of New Er3+ /Yb3+ -Codoped Tellurite Glasses
GAO Yuan, NIE Qiu-Hua, XU Tie-Feng, SHEN Xiang
College of Information Science and Engineering, Ningbo University, Ningbo 315211
Thermal Stability and Spectroscopic Properties of New Er3+ /Yb3+ -Codoped Tellurite Glasses
GAO Yuan;NIE Qiu-Hua;XU Tie-Feng;SHEN Xiang
College of Information Science and Engineering, Ningbo University, Ningbo 315211
关键词 :
73.43.Fj ,
74.25.Gz ,
73.61.Jc ,
76.30.Kg
Abstract : A series of new Er3+ /Yb3+ -codoped 70TeO2 --5Li2 O--(25-x)B2 O3 --xGeO2 (TLBG, x=0, 5, 10, 15, 20mol%) glasses are prepared. The thermal stability and spectroscopic properties of TLBG glasses are studied. It is found that these glasses have the better thermal stability ((Tx -Tg )>150 °C) compared with 75TeO2 --20ZnO--5Na2 O (TZN) glass. The fluorescence full width at half maximum (FWHM) is about 77nm, while the emission intensity and the quantum efficiency of the 4 I13/2 level of Er3+ increase with the increasing GeO2 content. The maximum quantum efficiency and stimulated emission cross-section of Er3+ calculated from the McCumber theory are 93.82% and 9.0×10-21 cm2 , respectively. The products of FWHM and σpeak e of Er3+ in TLBG glasses are larger than those in other reported glasses. The obtained data indicate that this kind of TLBG glasses is a promising candidate host material for Er3+ -doped broadband amplifiers.
Key words :
73.43.Fj
74.25.Gz
73.61.Jc
76.30.Kg
出版日期: 2004-09-01
:
73.43.Fj
(Novel experimental methods; measurements)
74.25.Gz
(Optical properties)
73.61.Jc
(Amorphous semiconductors; glasses)
76.30.Kg
(Rare-earth ions and impurities)
引用本文:
GAO Yuan;NIE Qiu-Hua;XU Tie-Feng;SHEN Xiang. Thermal Stability and Spectroscopic Properties of New Er3+ /Yb3+ -Codoped Tellurite Glasses[J]. 中国物理快报, 2004, 21(9): 1799-1801.
GAO Yuan, NIE Qiu-Hua, XU Tie-Feng, SHEN Xiang. Thermal Stability and Spectroscopic Properties of New Er3+ /Yb3+ -Codoped Tellurite Glasses. Chin. Phys. Lett., 2004, 21(9): 1799-1801.
链接本文:
https://cpl.iphy.ac.cn/CN/
或
https://cpl.iphy.ac.cn/CN/Y2004/V21/I9/1799
[1]
WANG Xun-Si;NIE Qiu-Hua;LIU Li-Ren;XU Tie-Feng;SHEN Xiang;DAI Shi-Xun;ZHANG Xiang-Hua. Improved Fluorescence from Tm3+ /Er3+ /Ce3+ Triply Doped Bismuth-Silicate Glasses for S+C-bands Amplifiers [J]. 中国物理快报, 2006, 23(9): 2553-2556.
[2]
WU Liang-Cai;LIU Bo;SONG Zhi-Tang;FENG Gao-Ming;FENG Song-Lin;CHEN Bomy. Total Dose Radiation Tolerance of Phase Change Memory Cell with GeSbTe Alloy [J]. 中国物理快报, 2006, 23(9): 2557-2559.
[3]
ZHANG Jian-Guo; WANG Xiao-Xin; CHENG Bu-Wen;YU Jin-Zhong; WANG Qi-Ming. Near Infrared Photoluminescence from Yb,Al Co-implanted SiO2 Films on Silicon [J]. 中国物理快报, 2006, 23(8): 2183-2186.
[4]
DAI Shi-Xun;XU Tie-Feng;NIE Qiu-Hua;SHEN Xiang;WANG Xun-Si. Concentration Quenching in Erbium Doped Bismuth Silicate Glasses [J]. 中国物理快报, 2006, 23(7): 1923-1925.
[5]
FANG Ying-Cui;ZHANG Zhuang-Jian;SHEN Jie;LU Ming. Photoluminescence from Electron-Beam Deposited CeO2 Thin Film after High Temperature Thermal Annealing [J]. 中国物理快报, 2006, 23(7): 1919-1922.
[6]
WANG Xiao-Xin;ZHANG Jian-Guo;CHENG Bu-Wen;YU Jin-Zhong;WANG Qi-Ming. Electroluminescence Afterglow from Indium Tin Oxide/Si-Rich SiO2 /p-Si Structure [J]. 中国物理快报, 2006, 23(5): 1306-1309.
[7]
XU Shi-Qing;FENG Ai-Ming;ZHANG Li-Yan;ZHAO Shi-Long;WANG Bao-Ling;ZHANG Jue;WANG Wei;BAO Ren-Qiang. Thermal Stability and Spectroscopic Properties of Yb3+ -Doped New Gallium--Lead--Germanate Glass [J]. 中国物理快报, 2006, 23(11): 3069-3071.
[8]
ZHANG Guo-Yong;ZHANG Peng-Xiang;ZHANG Hui;LEE Wing-Kee. Figure of Merit for Detectors Based on Laser-Induced hermoelectric Voltages in La1-x Cax MnO3 and Ba2 Cu3 O7-σ Thin Films [J]. 中国物理快报, 2005, 22(9): 2379-2381.
[9]
ZHANG Ting;LIU Bo;SONG Zhi-Tang;LIU Wei-Li;FENG Song-Lin;CHEN Bomy. Phase Transition Phenomena in Ultra-Thin Ge2 Sb2 Te5 Film [J]. 中国物理快报, 2005, 22(7): 1803-1805.
[10]
YU Hua;ZHAO Li-Juan;LIANG Qin;MENG Jie;YU Xuan-Yi;TANG Bai-Quan;TANG Li-Qin;XU Jing-Jun. Red Up-Conversion Luminescence Process in Oxyfluoride Glass Ceramics Doped with Er3+ /Yb3+ [J]. 中国物理快报, 2005, 22(6): 1500-1503.
[11]
ZHANG Lin-Li;GUO Chang-Xin;ZHAO Jun-Jing;HU Jun-Tao. Photoluminescence of Eu (III)-Doped ZnO Nanopowder and Energy Transfer from ZnO to Eu(III) Ions [J]. 中国物理快报, 2005, 22(5): 1225-1227.
[12]
XIA Ji-Lin;LIU Bo;SONG Zhi-Tang;FENG Song-Lin;CHEN Bomy. Electrical Properties of Ag-Doped Ge2 Sb2 Te5 Films Used for Phase Change Random Access Memory [J]. 中国物理快报, 2005, 22(4): 934-937.
[13]
TAO Wei-Dong;PAN Xue-Feng;CHEN Jian;YAN Fei-Biao;BAI Gui-Ru;LU Zu-Kang. Chiral Parameter of Transparent Films Containing Polymer Cholesteric Liquid Crystal-R [J]. 中国物理快报, 2005, 22(4): 931-933.
[14]
WANG Guo-Nian;DAI Shi-Xun;ZHANG Jun-Jie;XU Shi-Qing;HU Li-Li;JIANG Zhong-Hong. Fluorescence Lifetime Increasing with F- Ions into Ytterbium-Doped Germanium--Lead--Tellurite Glasses [J]. 中国物理快报, 2005, 22(2): 457-459.
[15]
YU Chun-Lei;DAI Shi-Xun;ZHOU Gang;ZHANG Jun-Jie;HU Li-Li;JIANG Zhong-Hong. Investigation on Nonradiative Decay of the Er3+ 4 I13/2 →4 I15/2 Transition in Different Tellurite Glass Matrix [J]. 中国物理快报, 2005, 22(11): 2926-2928.