Investigation on Nonradiative Decay of the Er3+4I13/2 →4I15/2 Transition in Different Tellurite Glass Matrix
YU Chun-Lei1, DAI Shi-Xun2, ZHOU Gang1, ZHANG Jun-Jie1, HU Li-Li1, JIANG Zhong-Hong1
1Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Sciences, Shanghai 201800
2College of Information Science and Engineering, Ningbo University, Ningbo 315211
Investigation on Nonradiative Decay of the Er3+4I13/2 →4I15/2 Transition in Different Tellurite Glass Matrix
1Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Sciences, Shanghai 201800
2College of Information Science and Engineering, Ningbo University, Ningbo 315211
Abstract: Three kinds of Er3-doped tellurite glasses with different hydroxyl groups are prepared by the conventional melt-quenching method. Infrared spectra are measured to estimate the exact content of OH- groups in samples. The maximum phonon energy in glasses are obtained by measuring the Raman scattering spectra. The strength parameters Ω5 (t=2,4,6) for all the samples are calculated and compared. The nonradiative decay rate of the Er3+4I13/2 → 4I15/2 transition are calculated for the glass samples with different phonon energy and OH- group contents. Finally, the effect of OH- groups on fluorescence decay rate of Er3+ is analysed, the constant KOH-Er of TWN, TZPL and TZL glasses are calculated to be 9.2×10-19cm4s-1, 5.9×10-19cm4s-1, and 3.5×10-19cm4s-1, respectively.
(Optical properties of bulk materials and thin films)