Utraviolet Lasing from ZnO Single Crystal at Room Temperature
XIANG Wang-Hua1;ZHANG Gui-Zhong1;SUN Yi2;WANG Gang2;John. B. Ketterson2
1College of Precision Instrument and Optoelectronics Engineering, Tianjin University, Tianjin 300072
2Department of Physics and Astronomy, Northwestern University, Evanston, IL60208 USA
Abstract: We experimentally studied ultraviolet photoluminescence (PL) from ZnO (0001) single crystal at room temperature. The PL spectra taken from the sample edge show spectral width narrowing; lifetime shortening (100 ps) and super linear intensity increase with pumping power, while the PL spectra taken from the sample surface only show broad spontaneous emission with a much longer lifetime ( > 5 ns). These findings suggest that stimulated emission and lasing were only achieved at edges of the ZnO single crystal. Scanning-electron-microscopic images show a smooth sample surface morphology and a rougher morphology at the single crystal edge. Electron-hole plasma enhancement of gain may be attributed to the lasing effect observed from the sample edge.
XIANG Wang-Hua;ZHANG Gui-Zhong;SUN Yi;WANG Gang;John. B. Ketterson. Utraviolet Lasing from ZnO Single Crystal at Room Temperature
[J]. 中国物理快报, 2003, 20(2): 296-297.
XIANG Wang-Hua, ZHANG Gui-Zhong, SUN Yi, WANG Gang, John. B. Ketterson. Utraviolet Lasing from ZnO Single Crystal at Room Temperature
. Chin. Phys. Lett., 2003, 20(2): 296-297.