High Efficiency Infrared-to-Visible Upconversion Emission in Er3+ ,Yb3+ , and Ho3+ Codoped Tellurite Glasses
DAI Shi-Xun1 , ZHANG Xiang-Hua2,1 , XU Tie-Feng1 , SHEN Xiang1 , WANG Xun-Shi1 , NIE Qiu-Hua1
1 College of Information Science and Engineering, Ningbo University, Ningbo 315211
2 Université de Rennes I, Rennes, France 35042
High Efficiency Infrared-to-Visible Upconversion Emission in Er3+ ,Yb3+ , and Ho3+ Codoped Tellurite Glasses
DAI Shi-Xun1 ;ZHANG Xiang-Hua2,1 ;XU Tie-Feng1 ;SHEN Xiang1 ;WANG Xun-Shi1 ;NIE Qiu-Hua1
1 College of Information Science and Engineering, Ningbo University, Ningbo 315211
2 Université de Rennes I, Rennes, France 35042
关键词 :
42.70.Ce ,
42.70.Hj ,
78.20.-e ,
78.55.-m
Abstract : A novel method of codoping the Er3+ , Yb3+ , and Ho3+ ions in tellurite glasses is demonstrated to obtain a high efficiency of infrared-to-visible upconversion. Three intense emission bands observed in Er3+ , Yb3+ , and Ho3+ codoped tellurite glasses centred at 525, 547, and 657nm correspond to Er3+ : 2 H11/2 → 4 I15/2 , Er3+ : 4 S3/2 → 4 I15/2 +Ho3+ : 5 S2 (5 F4 ) → 5 I8 , and Er3+ : 4 S3/2 0 → 4 I15/2 +Ho3+ : 5 F5 → 5 I8 transitions, respectively. No visible upconversion quenching phenomenon is observed when three rare-earth ions are codoped together in tellurite glasses. In contrast, the upconversion intensity of red and green emissions in Er3+ , Yb3+ , and Ho3+ codoped glasses is enhanced largely when compared with Er3+ /Yb3+ -codoped glasses. The dependence of upconversion intensities on excitation power and the possible upconversion mechanisms are evaluated. The three emissions are based on two-photon absorption processes.
Key words :
42.70.Ce
42.70.Hj
78.20.-e
78.55.-m
出版日期: 2006-07-01
:
42.70.Ce
(Glasses, quartz)
42.70.Hj
(Laser materials)
78.20.-e
(Optical properties of bulk materials and thin films)
78.55.-m
(Photoluminescence, properties and materials)
引用本文:
DAI Shi-Xun;ZHANG Xiang-Hua;XU Tie-Feng;SHEN Xiang;WANG Xun-Shi;NIE Qiu-Hua. High Efficiency Infrared-to-Visible Upconversion Emission in Er3+ ,Yb3+ , and Ho3+ Codoped Tellurite Glasses[J]. 中国物理快报, 2006, 23(7): 1810-1812.
DAI Shi-Xun, ZHANG Xiang-Hua, XU Tie-Feng, SHEN Xiang, WANG Xun-Shi, NIE Qiu-Hua. High Efficiency Infrared-to-Visible Upconversion Emission in Er3+ ,Yb3+ , and Ho3+ Codoped Tellurite Glasses. Chin. Phys. Lett., 2006, 23(7): 1810-1812.
链接本文:
https://cpl.iphy.ac.cn/CN/
或
https://cpl.iphy.ac.cn/CN/Y2006/V23/I7/1810
[1]
YANG Jian;QIU Tai;SHEN Chun-Ying. New BCN Fibres for Strong Ultraviolet and Visible Light Luminescence [J]. 中国物理快报, 2006, 23(9): 2573-2575.
[2]
ZHANG Ling;ZHANG Chun-Yu;WEI Zhi-Yi;ZHANG Zhi-Guo;Stephan Strohmaier;Hans J. Eichler. Characteristics of Nd:GdVO4 Laser with Different Nd-Doping Concentrations [J]. 中国物理快报, 2006, 23(8): 2088-2091.
[3]
LI Guang-Min;LI-Lan;WANG Da-Jian;ZHANG Xiao-Song;TAO Yi. Effect of Al3+ on Photoluminescence Properties of Eu3+ -Doped BaZr(BO3 )2 Phosphors [J]. 中国物理快报, 2006, 23(8): 2063-2065.
[4]
WANG Da-Jian;WANG Ji-Lei;LI Lan. Colour Tuning of Single Host Phosphors for White Light by Al Addition [J]. 中国物理快报, 2006, 23(8): 2247-2250.
[5]
SUN Cheng-Lin;LI Jian-Fu;HU Chang-Hong;JIANG Zhan-Kui;. Optical Properties of Pr3+ -Doped Y2 SiO5 Crystals [J]. 中国物理快报, 2006, 23(7): 1915-1918.
[6]
FANG Ying-Cui;ZHANG Zhuang-Jian;SHEN Jie;LU Ming. Photoluminescence from Electron-Beam Deposited CeO2 Thin Film after High Temperature Thermal Annealing [J]. 中国物理快报, 2006, 23(7): 1919-1922.
[7]
DAI Shi-Xun;XU Tie-Feng;NIE Qiu-Hua;SHEN Xiang;WANG Xun-Si. Concentration Quenching in Erbium Doped Bismuth Silicate Glasses [J]. 中国物理快报, 2006, 23(7): 1923-1925.
[8]
WANG Chun-Yu; JI Jiang-Hua; QI Yun-Feng;LOU Qi-Hong;ZHU Xiao-Lei; LU Yu-Tian. Kilohertz Electro-Optic Q-Switched Nd:YAG Ceramic Laser [J]. 中国物理快报, 2006, 23(7): 1797-1802.
[9]
CHEN Feng;WANG Xue-Lin;WANG Ke-Ming;WANG Lei;JIAO Yang;WANG Liang-Ling;LU Qing-Ming;MA Hong-Ji;NIE Rui. Optical Planar Waveguides in KTiOPO4 Crystals by MeV Oxygen Ion Implantation [J]. 中国物理快报, 2006, 23(6): 1501-1503.
[10]
QIAN Bo;CHEN San;CEN Zhan-Hong;CHEN Kun-Ji;LIU Yan-Song;XU Jun;MA Zhong-Yuan;LI Wei;HUANG Xin-Fan. Step-by-Step Laser Crystallization of Amorphous Si:H/SiNx :H Multilayer for Active Layer in Microcavities [J]. 中国物理快报, 2006, 23(5): 1302-1305.
[11]
LIANG Xin-Gang;HAN Mao-Hua. Experimental Study on Coherence of Thermal Radiation of Thin Film Structures [J]. 中国物理快报, 2006, 23(5): 1219-1221.
[12]
ZHOU Rui;DING Xin;WEN Wu-Qi;CAI Zhi-Qiang;WANG Peng;YAO Jian-Quan. High-Power Continuous-Wave Diode-End-Pumped Intracavity Frequency Doubled Nd:YVO4 Laser at 671nm with a Compact Three-Element Cavity [J]. 中国物理快报, 2006, 23(4): 849-851.
[13]
ZHANG Qin-Yuan; YANG Gang-Feng;JIANG Zhong-Hong;W. X. Que. Structural and Luminescence Properties of Transparent Nanocrystalline ZrO2 :Er3+ Films [J]. 中国物理快报, 2006, 23(4): 852-855.
[14]
JIANG Yi;WANG Ke-Ming;WANG Xue-Lin;JIA Chuan-Lei;ZHANG Jian-Xiu;WANG Ji-Yang;MA Hong-Ji;NIE Rui;SHEN Ding-Yu. Optical Waveguide Formed in Yb:KLu(WO4 )2 Crystal by 6.0MeV O+ Implantation [J]. 中国物理快报, 2006, 23(4): 922-924.
[15]
Akhlesh Lakhtakia;Tom G. Mackay. Dyadic Green Function for an Electromagnetic Medium Inspired by General Relativity [J]. 中国物理快报, 2006, 23(4): 832-833.