Topography of InP Surface Bombarded by O+ 2 Ion Beam
SUN Zhao-qi
Department of Physics, Anhui University, Hefei 230039
Topography of InP Surface Bombarded by O+ 2 Ion Beam
SUN Zhao-qi
Department of Physics, Anhui University, Hefei 230039
关键词 :
61.80.Jh
Abstract : The topography of InP surface bombarded by O+ 2 ion beam was investigated. Rippled topographies were observed for bombarded samples, and the data show that the ripple formation starts from a sputtering depth of about 0.4 μm. The wavelength and the disorder of the ripples both increase as the sputtering depth increases. The wavelength of the ripples appears to be sputtering depth dependent rather than sputtering rate dependent. It is confirmed that the ion- beam-induced surface rippling can be effectively suppressed by sample rotation during bombardment.
Key words :
61.80.Jh
出版日期: 1997-10-01
[1]
CHEN Feng;WANG Xue-Lin;WANG Ke-Ming;WANG Lei;JIAO Yang;WANG Liang-Ling;LU Qing-Ming;MA Hong-Ji;NIE Rui. Optical Planar Waveguides in KTiOPO4 Crystals by MeV Oxygen Ion Implantation [J]. 中国物理快报, 2006, 23(6): 1501-1503.
[2]
JIANG Yi;WANG Ke-Ming;WANG Xue-Lin;JIA Chuan-Lei;ZHANG Jian-Xiu;WANG Ji-Yang;MA Hong-Ji;NIE Rui;SHEN Ding-Yu. Optical Waveguide Formed in Yb:KLu(WO4 )2 Crystal by 6.0MeV O+ Implantation [J]. 中国物理快报, 2006, 23(4): 922-924.
[3]
CHEN Zhi-Quan;M. Maekawa;A. Kawasuso. Energy Variable Slow Positron Beam Study of Li+ -Implantation-Induced Defects in ZnO [J]. 中国物理快报, 2006, 23(3): 675-677.
[4]
LI Wei;MA Zhong-Quan;WANG Ye;WANG De-Ming. Optimization of Energy Scope for Titanium Nitride Films Grown by Ion Beam-Assisted Deposition [J]. 中国物理快报, 2006, 23(1): 178-181.
[5]
ZHU Xian-Fang;;WANG Zhan-Guo. Nanocavity Shrinkage and Preferential Amorphization during Irradiation in Silicon [J]. 中国物理快报, 2005, 22(3): 657-660.
[6]
HUANG Ning-Kang;WANG De-Zhi;ZHOU Ping;XIONG QI. X-Ray Photoelectron Spectroscopy Analysis of the Electron Beam
Treated SiC Films Before and After Hydrogen Ion Irradiation [J]. 中国物理快报, 2004, 21(1): 61-64.
[7]
WANG Shuang-Bao;ZHU Pei-Ran;WANG Yu-Guang;FENG Ke-An. Influences of H+ Implantation on the Boron-Doped Synthesized by Chemical Vapor Deposition Diamond Films [J]. 中国物理快报, 2000, 17(9): 686-688.
[8]
WANG Ke-ming;SHI Bo-rong;Nelson Cue;LU Fei;WANG Feng-xiang;XIE Zhao-xia;SHEN Ding-yu;LIU Yao-gang
. Splitting Behaviour of Implanted MeV Au+ Ions in LiB3 O5 [J]. 中国物理快报, 2000, 17(1): 40-42.
[9]
ZHAO Jun;MAO Dong-sheng;DING Xing-zhao;LIN Zi-xin;JIANG Bing-yao;YU Yue-hui;YANG Gen-qing;LIU Xiang-huai;S. Jin;H. Bender. Porous Structures and Short-Wavelength Photoluminescence of C+ -Implanted SiO2 Films [J]. 中国物理快报, 1999, 16(5): 361-363.
[10]
CHAI Jian-wei;YANG Guo-hua;PAN Hao-chang;CAO Jian-qing;
ZHU De-zhang;XU Hong-jie. Auger Electron Spectroscopy and Rut herford Backscattering-Channeling Study of Silicon Nitride Formation by Low Energy N+ 2 Ion Implantation [J]. 中国物理快报, 1999, 16(2): 120-122.
[11]
JIANG Lei;LIU Bo;ZHOU Zhu-ying;HE Mian-hong;ZHAO Guo-qing;ZONG Xiang-fu. In Situ Rutherford Backscattering Spectrometry Analysis of Films by Combination with Sputter Etching [J]. 中国物理快报, 1999, 16(10): 770-772.
[12]
MA Zhong-quan;LIU Bai-xin. Enhancement of Atomic Rearrangement in Top Surface Layers by Low Energy Ions [J]. 中国物理快报, 1998, 15(9): 668-670.
[13]
ZOU Zhi-qiang;FANG Hong-li;FU Xin-ding;CHEN Guo-ming. Fabricating Master with Reactive Ion Beam Etching Method [J]. 中国物理快报, 1998, 15(7): 495-497.
[14]
LI Xiangyang;CHENG Huansheng;YANG Fujia. Damage Production and Annealing During MeV He Ion RBS/Channeling Analysis of GaP
[J]. 中国物理快报, 1994, 11(4): 219-222.
[15]
BAI Haiyang;LIU Baixin. Irradiation Induced Amorphization and Free Energy Calculation in Immiscible Fe-Cu Multilayers
[J]. 中国物理快报, 1993, 10(9): 531-534.