Electrical and Pyroelectric Properties of Sol-Gel Derived (Pb,
Ca)TiO3 Thin Films with Various Orientations
TANG Xin-Gui1;DING Ai-Li2;CHAN Helen Lai-Wah1
1Department of Applied Physics and Materials Research Centre, The Hong Kong Polytechnic University, Hung Hom, Kowloon, Hong Kong
2Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050
Abstract: (Pb0.76Ca0.24)TiO3 (PCT) thin films with various orientations were grown on Pt/Ti/SiO2/Si substrates by using a sol-gel process and by controlling the temperature of heat-treatment. The PCT thin films with (100) and random orientation showed well-saturated hysteresis loops at an applied field of 800 kV/cm, with remanent polarisation and coercive electric field of 23.6 μC/cm2 and 225kV/cm, 17.8 μC/cm2 and 195 kV/cm, respectively. For highly (100)- and random-oriented PCT films, the dielectric constant and dielectric loss values of these films are 121 and 0.016, 121 and 0.024 at 1 kHz, respectively. The pyroelectric coefficients p of the PCT thin films are measured by a dynamic technique. At room temperature, the p values and figures of merits of the highly (100)- and random-oriented PCT films are 185 μC/m2K and 1.79 xm 10-5Pa-0.5, 176μC/m2K and 1.39 x 10-5Pa-0.5, respectively.
TANG Xin-Gui;DING Ai-Li;CHAN Helen Lai-Wah. Electrical and Pyroelectric Properties of Sol-Gel Derived (Pb,
Ca)TiO3 Thin Films with Various Orientations[J]. 中国物理快报, 2003, 20(11): 2039-2041.
TANG Xin-Gui, DING Ai-Li, CHAN Helen Lai-Wah. Electrical and Pyroelectric Properties of Sol-Gel Derived (Pb,
Ca)TiO3 Thin Films with Various Orientations. Chin. Phys. Lett., 2003, 20(11): 2039-2041.