Electrical and Pyroelectric Properties of Sol-Gel Derived (Pb,
Ca)TiO3 Thin Films with Various Orientations |
TANG Xin-Gui1;DING Ai-Li2;CHAN Helen Lai-Wah1 |
1Department of Applied Physics and Materials Research Centre, The Hong Kong Polytechnic University, Hung Hom, Kowloon, Hong Kong
2Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050 |
|
Cite this article: |
TANG Xin-Gui, DING Ai-Li, CHAN Helen Lai-Wah 2003 Chin. Phys. Lett. 20 2039-2041 |
|
|
Abstract (Pb0.76Ca0.24)TiO3 (PCT) thin films with various orientations were grown on Pt/Ti/SiO2/Si substrates by using a sol-gel process and by controlling the temperature of heat-treatment. The PCT thin films with (100) and random orientation showed well-saturated hysteresis loops at an applied field of 800 kV/cm, with remanent polarisation and coercive electric field of 23.6 μC/cm2 and 225kV/cm, 17.8 μC/cm2 and 195 kV/cm, respectively. For highly (100)- and random-oriented PCT films, the dielectric constant and dielectric loss values of these films are 121 and 0.016, 121 and 0.024 at 1 kHz, respectively. The pyroelectric coefficients p of the PCT thin films are measured by a dynamic technique. At room temperature, the p values and figures of merits of the highly (100)- and random-oriented PCT films are 185 μC/m2K and 1.79 xm 10-5Pa-0.5, 176μC/m2K and 1.39 x 10-5Pa-0.5, respectively.
|
Keywords:
77.84.-s
68.55.-a
77.22.Ch
|
|
Published: 01 November 2003
|
|
PACS: |
77.84.-s
|
(Dielectric, piezoelectric, ferroelectric, and antiferroelectric materials)
|
|
68.55.-a
|
(Thin film structure and morphology)
|
|
77.22.Ch
|
(Permittivity (dielectric function))
|
|
|
|
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|