Characterization of Growth Hillocks on the Surface of High-Pressure Synthetic Diamonds
YIN Long-Wei1 , LI Mu-Sen1 , YUAN Quan2 , XU Bin1 , HAO Zhao-Yin3
1 College of Materials Science and Engineering, Shandong University, Ji’nan 250061
2 College of Mechanical Science and Engineering, Shandong University, Ji’nan 250061
3 National Key Laboratory for Superhard Materials, Jilin University, Changchun 130012
Characterization of Growth Hillocks on the Surface of High-Pressure Synthetic Diamonds
YIN Long-Wei1 ;LI Mu-Sen1 ;YUAN Quan2 ;XU Bin1 ;HAO Zhao-Yin3
1 College of Materials Science and Engineering, Shandong University, Ji’nan 250061
2 College of Mechanical Science and Engineering, Shandong University, Ji’nan 250061
3 National Key Laboratory for Superhard Materials, Jilin University, Changchun 130012
关键词 :
81.10.-h ,
81.10.Aj ,
61.72.Hh ,
81.65.Cf ,
81.10.Dn
Abstract : Diamond crystals, with dimensions of about 0.5-0.6 mm, were synthesized in the presence of Fe-Ni and Fe-Ni-Si catalyst solvents under high-pressure-high-temperature (HPHT) conditions. The as-known dendritic pattern was clearly seen on the (111) or (100) planes of diamond single crystals grown using Fe-Ni as a catalyst solvent. However, the conventional dendritic pattern was not observed in diamonds grown in the presence of Fe-Ni-Si alloy catalyst. Trigonal-type, pyramid-type, polygonal-type, and rectangular-type growth hillocks were clearly observed on the (111) and (100) surfaces of diamonds grown from the Fe-Ni-Si-C system, and the density of the hillocks is very higher at some position. Clear successive growth layers can also be found on the (111) planes of the high-pressure diamond single crystals grown in the presence of Fe-Ni Si alloy catalyst. The growth hillocks distributing on the (111) and (100) planes of the diamonds generally occur on or near growth steps, and some of the hillocks terminate at certain solid inclusions and voids. Growth hillocks on the (111) and (100) surfaces directly indicate the spiral growth mechanism under high temperature-high pressure (HPHT). A possible formation process for growth hillocks is proposed.
Key words :
81.10.-h
81.10.Aj
61.72.Hh
81.65.Cf
81.10.Dn
出版日期: 2002-11-01
:
81.10.-h
(Methods of crystal growth; physics and chemistry of crystal growth, crystal morphology, and orientation)
81.10.Aj
(Theory and models of crystal growth; physics and chemistry of crystal growth, crystal morphology, and orientation)
61.72.Hh
(Indirect evidence of dislocations and other defects (resistivity, slip, creep, strains, internal friction, EPR, NMR, etc.))
81.65.Cf
(Surface cleaning, etching, patterning)
81.10.Dn
(Growth from solutions)
引用本文:
YIN Long-Wei;LI Mu-Sen;YUAN Quan;XU Bin;HAO Zhao-Yin. Characterization of Growth Hillocks on the Surface of High-Pressure Synthetic Diamonds[J]. 中国物理快报, 2002, 19(11): 1707-1710.
YIN Long-Wei, LI Mu-Sen, YUAN Quan, XU Bin, HAO Zhao-Yin. Characterization of Growth Hillocks on the Surface of High-Pressure Synthetic Diamonds. Chin. Phys. Lett., 2002, 19(11): 1707-1710.
链接本文:
https://cpl.iphy.ac.cn/CN/
或
https://cpl.iphy.ac.cn/CN/Y2002/V19/I11/1707
[1]
CHEN Wan-Chun;CHEN Xiao-Long. Chiral Symmetry Breaking During Growing Process of NaClO3 Crystal under Direct-Current Electric Field [J]. 中国物理快报, 2007, 24(1): 252-255.
[2]
ZHONG Fei;QIU Kai;LI Xin-Hua;YIN Zhi-Jun;XIE Xin-Jian;WANG Yang;JI Chang-Jian;CAO Xian-Cun;HAN Qi-Feng;CHEN Jia-Rong;WANG Yu-Qi. Effect of III/V Ratio of HT-AlN Buffer Layer on Polarity Selection and Electrical Quality of GaN Films Grown by Radio Frequency Molecular Beam Epitaxy [J]. 中国物理快报, 2007, 24(1): 240-243.
[3]
WANG Jian;TIAN Jian-Bai;XIONG Bing;SUN Chang-Zheng;HAO Zhi-Biao;LUO Yi. Deep InP Gratings for Opto-Electronic Devices Etched by Cl2 /CH4 /Ar Inductively Coupled Plasma [J]. 中国物理快报, 2006, 23(8): 2158-2160.
[4]
PAN Xiu-Hong;JIN Wei-Qing;HONG Yong;AI Fei. In Situ Observation of Skeletal Shape Transition during BaB2 O4 Crystal Growth in High-Temperature Solution [J]. 中国物理快报, 2006, 23(8): 2269-2272.
[5]
SU Zuo-Peng;DU Yong-Hui;JI Xiao-Rui;YANG Da-Peng;YANG Xu-Xin;GONG Xi-Liang;ZHANG Tie-Chen. Synthesis of Cubic Boron Nitride by the Reaction of Li3 N and B2 O3 [J]. 中国物理快报, 2006, 23(8): 2285-2287.
[6]
XIE Xin-Jian;ZHONG Fei;QIU Kai;LIU Gui-Feng;YIN Zhi-Jun;WANG Yu-Qi;LI Xin-Hua;JI Chang-Jian;HAN Qi-Feng;CHEN Jia-Rong;CAO Xian-Cun. Growth of Strain Free GaN Layers on (0001) Oriented Sapphire by Using Quasi-Porous GaN Template [J]. 中国物理快报, 2006, 23(6): 1619-1622.
[7]
LEE Chee-Wei;CHIN Mee-Koy. Room-Temperature Inductively Coupled Plasma Etching of InP Using Cl2 N2 and Cl2 /CH4 /H2 [J]. 中国物理快报, 2006, 23(4): 903-906.
[8]
LI Xin-Hua;XU Jia-Yue;JIN Min;SHEN Hui;LI Xiao-Min. Electrical and Optical Properties of Bulk ZnO Single Crystal Grown by Flux Bridgman Method [J]. 中国物理快报, 2006, 23(12): 3356-3358.
[9]
O. Sahin;N. Ucar. Creep Behaviour of Fe--Mn Binary Alloys [J]. 中国物理快报, 2006, 23(11): 3037-3040.
[10]
HONG Yong;AI Fei;PAN Xiu-Hong;JIN Wei-Qing;ZHONG Wei-Zhuo;SHINICHI Yoda. Growth of NaBi(WO4 )2 Dendrite and Mechanism [J]. 中国物理快报, 2006, 23(10): 2841-2844.
[11]
ZANG Chuan-Yi;JIA Xiao-Peng;MA Hong-An;LI Shang-Sheng;TIAN Yu;XIAO Hong-Yu. Grow Large High-Quality Diamonds with Different Seed Surfaces [J]. 中国物理快报, 2006, 23(1): 214-216.
[12]
ZANG Chuan-Yi;JIA Xiao-Peng;MA Hong-An;TIAN Yu;XIAO Hong-Yu. Effect of Regrown Graphite on the Growth of Large Gem Diamonds by Temperature Gradient Method [J]. 中国物理快报, 2005, 22(9): 2415-2417.
[13]
YU Ke;ZHANG Yong-Sheng;OUYANG Shi-Xi;ZHANG Qing-Jie;LUO Lai-Qiang;ZHANG Qiu-Xiang;CHANG Zhong-Kun;LI Li-Jun;ZHU Zi-Qiang. Synthesis and Field Emission of ZnO Nanostructures on CuO Catalyzed Porous Silicon Substrate [J]. 中国物理快报, 2005, 22(9): 2411-2414.
[14]
WANG Xian-Cheng;MA Hong-An;ZANG Chuan-Yi;TIAN Yu;LI Shang-Sheng;JIA Xiao-Peng;. Growth of Large High-Quality Type-II a Diamond Crystals [J]. 中国物理快报, 2005, 22(7): 1800-1802.
[15]
G. A. Gamal;M. Abou Zied;A. A. Ebnalwaled. Electronic Properties of Red P-Type Tl2 S5 Single Crystals [J]. 中国物理快报, 2005, 22(6): 1530-1532.