Grow Large High-Quality Diamonds with Different Seed Surfaces
ZANG Chuan-Yi, JIA Xiao-Peng, MA Hong-An, LI Shang-Sheng, TIAN Yu, XIAO Hong-Yu
The National Key Laboratory for Superhard Materials, Jilin University, Changchun 130012
Grow Large High-Quality Diamonds with Different Seed Surfaces
ZANG Chuan-Yi;JIA Xiao-Peng;MA Hong-An;LI Shang-Sheng;TIAN Yu;XIAO Hong-Yu
The National Key Laboratory for Superhard Materials, Jilin University, Changchun 130012
关键词 :
81.05.Uw ,
81.10.Aj ,
81.10.Dn ,
81.10.h
Abstract : Large high-quality type Ib diamond crystals have been grown with different seed surfaces by temperature gradient method at 5.5GPa, 1500--1600K, with NiMnCo alloy as the metal solvent. Compared with {100} as the growth surface, the growth region of large high-quality diamond crystals with {111} as the growth surface at a higher growth rate shifts markedly from lower temperatures (suitable for {100}-facet growth) to higher temperatures (suitable for {111}-facet growth). However, regardless of different growth surfaces, {100} or {111}, the grown crystals of sheet-shaped shape are most difficult for metal inclusions to be trapped into, and whether or not matched growth between the seed surfaces and the growth temperatures determines the crystal shapes. In view of the growth rates, large high-quality diamond crystals of sheet-shaped shapes can be grown at a growth rate of above 2.5mg/h, while the growth rate of large high-quality diamond c
Key words :
81.05.Uw
81.10.Aj
81.10.Dn
81.10.h
出版日期: 2006-01-01
:
81.05.Uw
81.10.Aj
(Theory and models of crystal growth; physics and chemistry of crystal growth, crystal morphology, and orientation)
81.10.Dn
(Growth from solutions)
81.10.h
引用本文:
ZANG Chuan-Yi;JIA Xiao-Peng;MA Hong-An;LI Shang-Sheng;TIAN Yu;XIAO Hong-Yu. Grow Large High-Quality Diamonds with Different Seed Surfaces[J]. 中国物理快报, 2006, 23(1): 214-216.
ZANG Chuan-Yi, JIA Xiao-Peng, MA Hong-An, LI Shang-Sheng, TIAN Yu, XIAO Hong-Yu. Grow Large High-Quality Diamonds with Different Seed Surfaces. Chin. Phys. Lett., 2006, 23(1): 214-216.
链接本文:
https://cpl.iphy.ac.cn/CN/
或
https://cpl.iphy.ac.cn/CN/Y2006/V23/I1/214
[1]
CHEN Wan-Chun;CHEN Xiao-Long. Chiral Symmetry Breaking During Growing Process of NaClO3 Crystal under Direct-Current Electric Field [J]. 中国物理快报, 2007, 24(1): 252-255.
[2]
WANG Yu;FANG Dai-Ning;SOH Ai-Kah;LIU Bin. Effects of Radius and Orientation of Single-Walled Carbon Nanotubes on Their Nonlinear Tensile Deformation Behaviour [J]. 中国物理快报, 2007, 24(1): 248-251.
[3]
WU Nan-Chun;XIA Yi-Ben;TAN Shou-Hong;WANG Lin-Jun;LIU Jian-Min;SU Qing-Feng. Influence of Positive Bias on Electrical Properties of Undoped Nanocrystalline Diamond Films [J]. 中国物理快报, 2006, 23(9): 2595-2597.
[4]
PAN Xiu-Hong;JIN Wei-Qing;HONG Yong;AI Fei. In Situ Observation of Skeletal Shape Transition during BaB2 O4 Crystal Growth in High-Temperature Solution [J]. 中国物理快报, 2006, 23(8): 2269-2272.
[5]
CHEN Guang-Chao;ZHOU Zu-Yuan;LI Bin;ZHOU You-Liang;J. Askri;LI Cheng-Ming;TANG Wei-Zhong;TONG Yu-Mei;LU Fan-Xiu. Behaviour of Self-Standing CVD Diamond Film with Different Dominant Crystalline Surfaces in Thermal-Iron Plate Polishing [J]. 中国物理快报, 2006, 23(8): 2266-2268.
[6]
LI Xin-Hua;XU Jia-Yue;JIN Min;SHEN Hui;LI Xiao-Min. Electrical and Optical Properties of Bulk ZnO Single Crystal Grown by Flux Bridgman Method [J]. 中国物理快报, 2006, 23(12): 3356-3358.
[7]
LI Chun-Yan;LI Bo;Lü Xian-Yi;LI Ming-Ji;WANG Zong-Li;GU Chang-Zhi;JIN Zeng-Sun. Superconductivity in Heavily Boron-Doped Diamond Films Prepared by Electron Assisted Chemical Vapour Deposition Method [J]. 中国物理快报, 2006, 23(10): 2856-2858.
[8]
HONG Yong;AI Fei;PAN Xiu-Hong;JIN Wei-Qing;ZHONG Wei-Zhuo;SHINICHI Yoda. Growth of NaBi(WO4 )2 Dendrite and Mechanism [J]. 中国物理快报, 2006, 23(10): 2841-2844.
[9]
ZANG Chuan-Yi;JIA Xiao-Peng;MA Hong-An;TIAN Yu;XIAO Hong-Yu. Effect of Regrown Graphite on the Growth of Large Gem Diamonds by Temperature Gradient Method [J]. 中国物理快报, 2005, 22(9): 2415-2417.
[10]
YU Ke;ZHANG Yong-Sheng;OUYANG Shi-Xi;ZHANG Qing-Jie;LUO Lai-Qiang;ZHANG Qiu-Xiang;CHANG Zhong-Kun;LI Li-Jun;ZHU Zi-Qiang. Synthesis and Field Emission of ZnO Nanostructures on CuO Catalyzed Porous Silicon Substrate [J]. 中国物理快报, 2005, 22(9): 2411-2414.
[11]
WANG Xian-Cheng;MA Hong-An;ZANG Chuan-Yi;TIAN Yu;LI Shang-Sheng;JIA Xiao-Peng;. Growth of Large High-Quality Type-II a Diamond Crystals [J]. 中国物理快报, 2005, 22(7): 1800-1802.
[12]
ZHANG Ming-Long;XIA Yi-Ben;WANG Lin-Jun;GU Bei-Bei. Characterization of Defects in Chemical Vapour Deposited Diamonds [J]. 中国物理快报, 2005, 22(5): 1264-1266.
[13]
XU Bin;CUI Jian-Jun;LI Mu-Sen;LI Cheng-Mei;CHU Fu-Min;FENG Li-Ming. Carbide Identification in Different Regions of a Thin Metal Film Covering on an HPHT As-Grown Diamond Single Crystal from Ni--Mn--C System [J]. 中国物理快报, 2005, 22(2): 478-481.
[14]
WU Nan-Chun;XIA Yi-Ben;TAN Shou-Hong;WANG Lin-Jun. Effect of Gas Pressure on Nanocrystalline Diamond Films Prepared by Electron-Assisted Chemical Vapour Deposition [J]. 中国物理快报, 2005, 22(11): 2969-2972.
[15]
CHEN Wan-Chun;LIU Dao-Dan;WANG YU-Ren. Morphological Evolution during Synthesis of New AlPO4 .H2 O Crystal [J]. 中国物理快报, 2005, 22(10): 2704-2707.