Broadband Infrared Luminescence of Ni 2+ in Petalite-Type Transparent Glass Ceramics |
FENG Gao-Feng;ZHOU Shi-Feng;ZHANG Song-Min;YANG Hu-Cheng;QIU Jian-Rong |
State Key Laboratory of Silicon Materials, Zhejiang University, Hangzhou 310027 |
|
Cite this article: |
FENG Gao-Feng, ZHOU Shi-Feng, ZHANG Song-Min et al 2007 Chin. Phys. Lett. 24 968-970 |
|
|
Abstract Transparent Ni 2+ -doped magnesium aluminosilicate glass ceramics are prepared. The formation of petalite-type crystallites in the glass ceramics is confirmed by x-ray diffraction. Broadband infrared luminescence centred at around 1235nm with full width at half maximum (FWHM) of about 300nm is observed from the Ni 2+ -doped glass ceramics. The observed infrared emission could be attributed to the 3T 2(F) →3 A 2(F) transition of octahedral Ni 2+ ions in petalite-type crystallites. The product of the fluorescence lifetime and the stimulated emission cross sections is 1.2×10 -24 cm 2s.
|
Keywords:
42.70.Hj
42.79.Sz
33.50.Dq
|
|
Received: 20 November 2006
Published: 26 March 2007
|
|
PACS: |
42.70.Hj
|
(Laser materials)
|
|
42.79.Sz
|
(Optical communication systems, multiplexers, and demultiplexers?)
|
|
33.50.Dq
|
(Fluorescence and phosphorescence spectra)
|
|
|
|
|
[1] Beall G H and Pinckney L R 1999 J. Am. Ceram. Soc. 82 5 [2] Pinckney L R 1999 J. Non-Cryst. Solids 255 171 [3] Samson B N et al 2002 Opt. Lett. 27 1309 [4] Reisfeld R et al 1984 Chem. Phys.Lett. 104 153 [5] Buch A et al 1985 Mater. Sci. Eng. 71 383 [6] Reisfeld R 1985 Mater. Sci. Eng. 71 375 [7] Andrews L J, Beall G H and Lempicki A 1986 J. Lumin. 3665 [8] Suzuki T and Ohishi Y 2004 Appl. Phys. Lett. 84 3804 [9] Suzuki T, Murugan G S and Ohishi Y 2005 Appl. Phys. Lett. 86 131903 [10] Suzuki T, Horibuchi K and Ohishi Y 2005 J. Non-Cryst.Solids 351 2304 [11] Zhou S F, Feng G F et al 2006 Chin. Phys. Lett. 232996 [12] Schreyer W and Schairer J F 1962 Am. Mineral. 47 90 [13] Galoisy L and Galas G 1993 Geochim. Cosmochim. Acta 573613 [14] Reisfeld R, Kisilev A, Buch A et al 1987 J. Non-Cryst.Solids 91 333 [15] Tanabe Y and Sugano S 1954 J. Phys. Soc. Jpn. 9 753,766 [16] Kuleshov N V et al 1997 J. Lumin. 71 265 [17] Albers P, Stark E and Park S H 1985 J. Opt. Soc. Am. B 3 134 |
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|