YBa2Cu3O7 Bicrystal Josephson Junctions and dc SQUIDs |
Yu. V. Kislinskii1;ZHAO Bai-ru;WU Pei-jun;PENG Zhi-qiang;CHEN Ying-fei;YANG Tao;CHEN Lie;SUN Ji-jun;XU Bo;WU Fei;ZHOU Yue-liang;LI Lin;ZHAO Zhong-xian;E. A. Stepantsov2 |
Institute of physics, Chinese Academy of Sciences, Beijing 100080
1Permanent address : Institute of Crystallography, 117333, Moscow, Russia
2Institute of Crystallography, 117333, Moscow, Russia
|
|
Cite this article: |
Yu. V. Kislinskii, ZHAO Bai-ru, WU Pei-jun et al 1996 Chin. Phys. Lett. 13 390-393 |
|
|
Abstract Bicrystal Josephson junctions and direct current superconducting quantum interference devices ( dc SQUIDs) were prepares on YBa2Cu3O7( YBCO ) thin films deposited on yttrium stabilized ZrO2 bicrystal substrates The critical current densities Jc ~ 2 X 106 A/cm2 for YBCO thin film and (1 - 3 ) X 103 A/cm2 at boundaries were obtained at 77K. For YBCO Josephson junction made on 28°misorientated boundary, the Shapiro steps were observed. The dc SQUID was made on the 32° misorientated boundary junctions, which consisted of 40 X 40μm of loop and 2000 X 2000μm planar superconductive flux focuser. The voltage modulation depth of this SQUID was 6μV, and the magnetic field sensitivity was estimated to be ~ 2pT /√Hz from the measured noise level.
|
Keywords:
74.50.+r
74.76.Bz
74.90.+n
|
|
Published: 01 May 1996
|
|
|
|
|
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|