摘要Magnetic and magneto-transport properties of nano-structured CoO-Ag granular films are reported. Apparent magnetization hysteresis is observed for low CoO contents and becomes weaker with increasing CoO content. Magnetoresistance (MR) ratio has a maximal value near 84vol% CoO and is reduced at low CoO contents. It decreases with increasing temperature and disappears near the Néel temperature of CoO. The uncompensated magnetic moments of CoO particles have been clearly demonstrated by MR effect.
Abstract：Magnetic and magneto-transport properties of nano-structured CoO-Ag granular films are reported. Apparent magnetization hysteresis is observed for low CoO contents and becomes weaker with increasing CoO content. Magnetoresistance (MR) ratio has a maximal value near 84vol% CoO and is reduced at low CoO contents. It decreases with increasing temperature and disappears near the Néel temperature of CoO. The uncompensated magnetic moments of CoO particles have been clearly demonstrated by MR effect.
[1] Jacobs I S and Bean C P 1963 Magnetism ed Rado G T and Suhl H (New York: Academic) vol III p 294[2] Kodama R H, Makhlouf S A and Berkowitz A E 1997 Phys. Rev. Lett. 79 1393[3] Kodama R H and Berkowitz A E 1999 Phys. Rev. B 59 6321[4] Punnoose A, Magnone H, Seehra M S and Bonevich J 2001 Phys. Rev. B 64 174420[5] Punnoose A and Seehra M S 2002 J. Appl. Phys. 91 7766[6] Schuele W J and Deetsereek V D 1962 J. Appl. Phys. 33 1136[7] Richardson J T, Yiagas D I, Turk B, Forster K and Twigg M V 1991 J. Appl. Phys. 70 6977[8] Ambrose T and Chien C L 1996 Phys. Rev. Lett. 76 1743[9] Néel L 1962 Low Temperature Physics ed DeWitt C, Dreyfus B and Gennes P D D (New York: Gordon and Breach) p 413[10] Martí X et al 2012 Phys. Rev. Lett. 108 017201[11] Del Bianco L, Spizzo F, Tamisari M and Castiglioni A 2011 J. Appl. Phys. 110[12] Berkowitz A E et al 1992 Phys. Rev. Lett. 68 3745[13] Xiao J Q, Jiang J S, and Chien C L 1992 Phys. Rev. Lett. 68 3749[14] Parkin S S P, 1995 Annu. Rev. Mater. Sci. 25 357[15] Nesbet R K 1998 IBM J. Res. Dev. 42 53[16] Wang L, Wang S G, Rizwan S, Qin Q H and Han X F 2009 Appl. Phys. Lett. 95 152512[17] Park B G et al 2011 Nature Mater. 10 347[18] See, e.g., Nagamiya T, Yosida K and Kubo R 1955 Adv. Phys. 4 1[19] Xiong P, Xiao G, Wang J Q, Xiao J Q, Jiang J S and Chien C L 1992 Phys. Rev. Lett. 69 3220[20] Yu-Zhang K, Imhoff D, Leprince-Wang Y et al 2003 Acta Mater. 51 1157[21] Kondo J 1969 Solid State Phys. 23 184[22] Makhlouf S A, Parker F T and Berkowitz A E 1997 Phys. Rev. B 55 R14717[23] Seehra M S, Babu V S, Manivannan A and Lynn J W 2000 Phys. Rev. B 61 3513[24] Chien C L 1995 Annu. Rev. Mater. Sci. 25 129[25] Wang J Q and Xiao G 1994 Phys. Rev. B 49 3982
2012, Vol. 29 