摘要The growth rate of diamond has been investigated for a long time and researchers have been attempting to enhance the growth rate of high-quality gem diamond infinitely. However, it has been found according to previous research results that the quality of diamond is debased with the increase of growth rate. Thus, under specific conditions, the growth rate of high-quality diamond cannot exceed a limited value that is called the limited growth rate of diamond. We synthesize a series of type Ib gem diamonds by temperature gradient method under high pressure and high temperature (HPHT) using the as-grown {100} face. The dependence of limited growth rate on growth conditions is studied. The results show that the limited growth rate increases when synthetic temperature decreases, also when growth time is prolonged.
Abstract：The growth rate of diamond has been investigated for a long time and researchers have been attempting to enhance the growth rate of high-quality gem diamond infinitely. However, it has been found according to previous research results that the quality of diamond is debased with the increase of growth rate. Thus, under specific conditions, the growth rate of high-quality diamond cannot exceed a limited value that is called the limited growth rate of diamond. We synthesize a series of type Ib gem diamonds by temperature gradient method under high pressure and high temperature (HPHT) using the as-grown {100} face. The dependence of limited growth rate on growth conditions is studied. The results show that the limited growth rate increases when synthetic temperature decreases, also when growth time is prolonged.
[1] Strong H M and Wentorf R H Jr 1972 Naturwissenschaften 59 1 [2] Strong H M and Chrenko R M 1971 J. Phys. Chem. 75 1838 [3] Tian Y and Ma H A et al 2006 Diamond and AbrasivesEngineering 151 5 [4] Sumiya H, Toda N and Satoh S 2002 J. Crystal Growth 237-2391281 [5] Sumiya H and Satoh S 1996 Diamond Relat. Mater. 5 1359 [6] Sumiya H, Toda N and Satoh S 2000 New Diamond Frontier CarbonTech. 10 233 [7] Burns R C et al 1999 Diamond Relat. Mater. 8 1433 [8] Kiflawi I et al 2002 Diamond Relat. Mater. 11 204 [9] Jia X P et al 1999 Diamond Relat. Mater. 8 1895 [10] Zang C Y et al 2004 Chin. Phys. Lett. 21 1684 [11] Wang X C et al 2005 Chin. Phys. Lett. 22 1800 [12] Ho S S et al Industrial Diamond Rev. 28-32
2007, Vol. 24 