Effects of NaN3 Added in Fe-C System on Inclusion and Impurity of Diamond Synthesized at High Pressure and High Temperature
LIANG Zhong-Zhu1, LIANG Jing-Qiu1, JIA Xiao-Peng2
1National Key Laboratory of Applied Optics, Changchun Institute of Optics, Fine Mechanics and Physics, Chinese Academy of Sciences, Changchun 1300332National Lab of Superhard Materials, Jilin University, Changchun 130012
Effects of NaN3 Added in Fe-C System on Inclusion and Impurity of Diamond Synthesized at High Pressure and High Temperature
LIANG Zhong-Zhu1, LIANG Jing-Qiu1, JIA Xiao-Peng2
1National Key Laboratory of Applied Optics, Changchun Institute of Optics, Fine Mechanics and Physics, Chinese Academy of Sciences, Changchun 1300332National Lab of Superhard Materials, Jilin University, Changchun 130012
摘要Effects of NaN3 added in Fe-C system to synthesize nitric diamond at high pressure and high temperature are investigated. Diamond crystals with high nitrogen concentration are synthesized by the system of Fe-C and NaN3 additive at pressure 5.8GPa and at temperatures 1750-1780K for 15min. The synthetic diamond crystals have a cubo-octahedral or octahedral shape with yellowish green or green colour. Some disfigurements are observed on the surfaces of most diamond crystals. The composition and content of inclusions formed by iron in diamond are changed and iron nitride is detected in diamond crystals synthesized with Fe-C-NaN3 additive. As the amount of NaN3 additive increases, Fe3C decreases and iron nitride increases with α-Fe being nearly constant. Moreover, the nitrogen concentrations in diamond crystals synthesized with 1.5wt% NaN3 additive is up to 2250ppm in substitutional form.
Abstract：Effects of NaN3 added in Fe-C system to synthesize nitric diamond at high pressure and high temperature are investigated. Diamond crystals with high nitrogen concentration are synthesized by the system of Fe-C and NaN3 additive at pressure 5.8GPa and at temperatures 1750-1780K for 15min. The synthetic diamond crystals have a cubo-octahedral or octahedral shape with yellowish green or green colour. Some disfigurements are observed on the surfaces of most diamond crystals. The composition and content of inclusions formed by iron in diamond are changed and iron nitride is detected in diamond crystals synthesized with Fe-C-NaN3 additive. As the amount of NaN3 additive increases, Fe3C decreases and iron nitride increases with α-Fe being nearly constant. Moreover, the nitrogen concentrations in diamond crystals synthesized with 1.5wt% NaN3 additive is up to 2250ppm in substitutional form.
(Impurity doping, diffusion and ion implantation technology)
引用本文:
LIANG Zhong-Zhu;LIANG Jing-Qiu;JIA Xiao-Peng. Effects of NaN3 Added in Fe-C System on Inclusion and Impurity of Diamond Synthesized at High Pressure and High Temperature[J]. 中国物理快报, 2009, 26(3): 38104-038104.
LIANG Zhong-Zhu, LIANG Jing-Qiu, JIA Xiao-Peng. Effects of NaN3 Added in Fe-C System on Inclusion and Impurity of Diamond Synthesized at High Pressure and High Temperature. Chin. Phys. Lett., 2009, 26(3): 38104-038104.
[1] Wentorf R H 1971 J. Phys. Chem. 75 1833 [2] Strong H M and Chrenko R M 1971 J. Phys. Chem. 75 1838 [3] Yin L W, Li M S, Sun D S and Cui J J 2001 Mater.Lett. 48 21 [4] Ekimov E A, Sidorov V A, Bauer E D, Mel'nik N N, Curro NJ, Thompson J D and Stishov S M 2004 Nature 4 428 [5] Kalish R 1999 Carbon 37 781 [6] Li S S, Jia X, Zang C Y, Tian Y, Zhang Y F, Xiao H Y andHuang G F 2008 Chin. Phys. Lett. 25 3801 [7] Shih C F, Liu K S and Lin I N 2000 Diamond Relat.Mater. 9 1591 [8] Seo S H , Lee T, Kim Y, Park C and Park J 2004 ThinSolid Films 447 212 [9] Reinitz I M, Fritsch E and Shigley J E 1998 DiamondRel. Mater. 7 133 [10] Collins A T, Kanda H and Kitawaki H 2000 DiamondRel. Mater. 9 113 [11] Kanda H, Akaishi M and Yamaoka S 1999 Diamond Relat.Mater. 8 1441 [12] Liang Z Z, Jia X, Zang C Y, Zhu P W, Ma H A and Ren G Z2005 Diamond Rel. Mater. 14 243 [13] Kanda H, Akaishi M, Setaka N, Yamaoka S and Fukunaga O1980 J. Mater. Sci. 15 2743 [14] Liang Z Z, Jia X, Zhu P W, Ma H A, Zang C Y, Qing J Mand Guan Q F 2006 Diamond Rel. Mater. 15 10 [15] Liang Z Z, Jia X and Liang J Q 2007 Chin. Phys.Lett. 24 3551 [16] Jia X, Hayakawa S, Li W, Gohshi Y and Wakatsuki M 1999 Diamond Rel. Mater. 8 1895 [17] Kopcewicz M, Jagielski J, Turos A and Williamson D L1992 J Appl. Phys. 71 4217
2009, Vol. 26 