Fabrication and Characterization of Single-Crystalline AgSbTe Nanowire Arrays |
YANG You-Wen1**, LI Tian-Ying1, ZHU Wen-Bin1, MA Dong-Ming1, CHEN Dong2 |
1School of Chemical Engineering, Hefei University of Technology, Hefei 230009 2School of Instrument Science and Opto-electronics Engineering, Hefei University of Technology, Hefei 230009
|
|
Cite this article: |
YANG You-Wen, LI Tian-Ying, ZHU Wen-Bin et al 2013 Chin. Phys. Lett. 30 108102 |
|
|
Abstract Ternary semiconducting AgSbTe2 nanowire arrays were synthesized for the first time by using the direct-current electrodeposition technique. X-ray diffraction, scanning electron microscopy, energy dispersive spectrometry, and transmission electron microscopy analyses indicate that the nanowire arrays are high filling, ordered, single crystalline and the nanowires have a highly preferential orientation grown along the [100] direction. Annealing studies show that compared with other temperatures, annealing at 100°C can significantly increase the crystallinity of AgSbTe2 nanowires. The optical absorbance spectra of the AgSbTe2 nanowire arrays show that the optical band gap has a strong blue shift with decreasing the diameter of the nanowire.
|
|
Received: 08 May 2013
Published: 21 November 2013
|
|
|
|
|
|
[1] Chen N, Gascoin F, Snyder G J, Muller E, Karpinski G and Stiewe C 2005 Appl. Phys. Lett. 87 171903 [2] Detemple R, Wamwangi D, Wuttig M and Bihlmayer G 2003 Appl. Phys. Lett. 83 2572 [3] Wernick J H and Benson K E 1957 J. Phys. Chem. Solids 3 157 [4] McHugh J P, Tiller W A, Haszko S E and Wernick J H 1961 J. Appl. Phys. 32 1785 [5] Berri S, Maouche D and Medkour Y 2012 Physica B 407 3320 [6] Wang H, Li J F, Zou M and Sui T 2008 Appl. Phys. Lett. 93 202106 [7] Zayed H A, Ibrahim A M and Soliman L I 1996 Vacuum 47 49 [8] Abdelghany A, Elsayed S N, El Ela A H and Mousa N H 1996 Vacuum 47 243 [9] Wolfe R, Wernick J H and Haszko S E 1960 J. Appl. Phys. 31 1959 [10] Du B, Li H, Xu J, Tang X and Uher C 2010 Chem. Mater. 22 5521 [11] Ma H, Su T, Zhu P, Guo J and Jia X 2008 J. Alloys Compd. 454 415 [12] Sugar J D and Medlin D L 2009 J. Alloys Compd. 478 75 [13] Zhang S N, Zhu T J, Yang S H, Yu C and Zhao X B 2010 J. Alloys Compd. 499 215 [14] Sugar J D and Medlin D L 2011 J. Mater. Sci. 46 1668 [15] Hoang K, Mahanti S D, Salvador J R and Kanatzidis M G 2007 Phys. Rev. Lett. 99 156403 [16] Sha J, Niu J, Ma X, Xu J, Zhang X, Yang Q and Yang D 2002 Adv. Mater. 14 1219 [17] Yang Q, Sha J, Xu J and Yang D 2003 Chem. Phys. Lett. 379 87 [18] Gao H, Gao D Q and Xue D S 2011 Chin. Phys. B 20 057502 [19] Park K, Xiao F, Yoo B Y, Rheem Y and Myung N V 2009 J. Alloys Compd. 485 362 [20] Ye L H, Hoang K, Freeman A J, Mahanti S D, He J, Tritt T M and Kanatzidis M G 2008 Phys. Rev. B 77 245203 [21] Athauda T J, Hari P and Ozer R R 2013 ACS Appl. Mater. Interfaces 5 6237 [22] Zhang X, Liu D, Zhang L, Li W, Gao M, Ma W, Ren Y, Zeng Q, Niu Z, Zhou W and Xie S 2009 J. Mater. Chem. 19 962 |
|