Optical Waveguide Formed in RbTiOPO4 Crystal by 6.0 MeV O3+ Implantation
JIAO Yang1;WANG Ke-Ming1;WANG Xue-Lin1;CHEN Feng1; WANG Lei1;WANG Liang-Ling1;LU Qing-Ming2;MA Hong-Ji3;NIE Rie3
¹School of Physics and Microelectronics, Shandong University, Jinan 250100 ²School of Chemistry and Chemical Engineering, Shandong University, Jinan 250100 ³The Key Laboratory of Heavy Ion Physics of Ministry of Education, Peking University, Beijing 100871
Cite this article:   
JIAO Yang, WANG Ke-Ming, WANG Xue-Lin et al  2006 Chin. Phys. Lett. 23 3328-3330
Download: PDF(242KB)  
Export: BibTeX | EndNote | Reference Manager | ProCite | RefWorks
Abstract A planar optical waveguide was formed in RbTiOPO4; crystal by 6.0-MeV oxygen ion implantation with the dose of 2×1015 ions/cm² at room temperature. Annealing at 200°C for 30 min in air is performed to improve the thermal stability of the waveguide. The dark modes of the waveguide are measured at wavelengths 633 and 1539 nm, respectively. The refractive index profiles in the guiding layer are reconstructed by using the reflectivity calculation method. TRIM'98 code was carried out to simulate the damage profiles caused by the implantation process to obtain a better understanding of the waveguide formation.



Keywords: 61. 80. Jh      42. 79. Gn      42. 82. Et     
Published: 01 December 2006
PACS:  61. 80. Jh  
  42. 79. Gn  
  42. 82. Et  
TRENDMD:   
URL:  
https://cpl.iphy.ac.cn/       OR      https://cpl.iphy.ac.cn/Y2006/V23/I12/03328
Service
E-mail this article
E-mail Alert
RSS
Articles by authors
JIAO Yang
WANG Ke-Ming
WANG Xue-Lin
CHEN Feng
WANG Lei
WANG Liang-Ling
LU Qing-Ming
MA Hong-Ji
NIE Rie
Viewed
Full text


Abstract