Absorption Spectra and Ionic Conductivity of RbxCs1-xAg4I5 Superionic Conductors Thin Films
CAO Yang1;SUN Jia-Lin1;ZHANG Guo-Sheng2;GUO Ji-Hua1;WANG Zheng-Ping2
1Key Laboratory of Atomic and Molecular Nanosciences of Education Ministry and Department of Physics, Tsinghua University, Beijing 100084 2Department of Physics, Science School, Harbin Engineering University, Harbin 150001
Cite this article:   
CAO Yang, SUN Jia-Lin, ZHANG Guo-Sheng et al  2005 Chin. Phys. Lett. 22 239-242
Download: PDF(621KB)  
Export: BibTeX | EndNote | Reference Manager | ProCite | RefWorks
Abstract A series of RbxCs1-xAg4I5 (x=0--1) thin films were grown by vacuum evaporation on NaCl crystal substrates at 350K. The absorption spectra of these films were measured at 80K in the wavelength range from 240nm to 400nm. It is shown that superionic conductor thin films of quaternary compound Rb0.5Cs0.5Ag4I5 and ternary compound RbAg4I5 can be obtained at x=0.5--0.6 and x=0.7--1, respectively. At x=0.65, the combined compound film of the mixture of 30mol\% RbAg4I5 and 70mol% Rb0.5Cs0.5Ag4I5 is presented. Then, based on the spectral positions of the A1 and A2 peaks, we determined that the Rb0.5Cs0.5Ag4I5 exciton coupling energy Rex is 0.21eV, the forbidden zone width Eg is 3.82eV and the exciton radius aex is 0.70nm. Furthermore, the ionic conductivities of superionic conductor thin films of RbAg4I5 and Rb0.5Cs0.5Ag4I5 and their mixture film are investigated, respectively, in the temperature range 303K--393K.
Keywords: 81.15.Ef      68.55.Nq      78.20.-e     
Published: 01 January 2005
PACS:  81.15.Ef  
  68.55.Nq (Composition and phase identification)  
  78.20.-e (Optical properties of bulk materials and thin films)  
TRENDMD:   
URL:  
https://cpl.iphy.ac.cn/       OR      https://cpl.iphy.ac.cn/Y2005/V22/I1/0239
Service
E-mail this article
E-mail Alert
RSS
Articles by authors
CAO Yang
SUN Jia-Lin
ZHANG Guo-Sheng
GUO Ji-Hua
WANG Zheng-Ping
Related articles from Frontiers Journals
[1] HU Guo-Hang, ZHAO Yuan-An, LI Da-Wei, XIAO Qi-Ling. Wavelength Dependence of Laser-Induced Bulk Damage Morphology in KDP Crystal: Determination of the Damage Formation Mechanism[J]. Chin. Phys. Lett., 2012, 29(3): 239-242
[2] XIANG Xia, SHI Xiao-Yan, GAO Xiao-Lin, JI Fang, WANG Ya-Jun, LIU Chun-Ming, ZU Xiao-Tao. Effect of N-Doping on Absorption and Luminescence of Anatase TiO2 Films[J]. Chin. Phys. Lett., 2012, 29(2): 239-242
[3] DOU Fei, ZHANG Xin-Ping** . Charge Transfer Channels in Formation of Exciplex in Polymer Blends[J]. Chin. Phys. Lett., 2011, 28(9): 239-242
[4] CHEN Heng-Zhi, YANG Bin**, SUN Yan, ZHANG Ming-Fu, WANG Zhu, ZHANG Rui, ZHANG Zhi-Guo, CAO Wen-Wu, . Optical Temperature Sensor Using Infrared-to-Visible-Frequency Upconversion in Er 3+/Yb 3+−Codoped Bi3TiNbO9 Ceramics[J]. Chin. Phys. Lett., 2011, 28(8): 239-242
[5] XU Cheng, **, XU Lin-Min, ZHANG Han-Zhuo, QIANG Ying-Huai, ZHU Ya-Bo, LIU Jiong-Tian, SHAO Jian-Da . Comparative Studies on the Laser Damage Resistance of Ta2O5 and Nb2O5 Films Performed under Different Electron Beam Currents[J]. Chin. Phys. Lett., 2011, 28(6): 239-242
[6] CHEN Yi-Xin**, SHEN Guang-Di, ZHU Yan-Xu, GUO Wei-Ling, LI Jian-Jun . Efficiency-enhanced AlGaInP Light-Emitting Diodes with Thin Window Layers and Coupled Distributed Bragg Reflectors[J]. Chin. Phys. Lett., 2011, 28(6): 239-242
[7] ZHAN Feng**, WANG Hai-Li, HE Ji-Fang, WANG Juan, HUANG She-Song, NI Hai-Qiao, NIU Zhi-Chuan . Multilayer Antireflection Coating for Triple Junction Solar Cells[J]. Chin. Phys. Lett., 2011, 28(4): 239-242
[8] LUO Hao, WANG Tao, GONG Rong-Zhou**, NIE Yan, WANG Xian . Extending the Bandwidth of Electric Ring Resonator Metamaterial Absorber[J]. Chin. Phys. Lett., 2011, 28(3): 239-242
[9] LIU Chun-Ming**, XIANG Xia, ZHANG Yan, JIANG Yong, ZU Xiao-Tao . Magnetism of a Nitrogen-Implanted TiO2 Single Crystal[J]. Chin. Phys. Lett., 2011, 28(12): 239-242
[10] HUANG Jian**, WANG Lin-Jun, TANG Ke, XU Run, ZHANG Ji-Jun, LU Xiong-Gang, XIA Yi-Ben . Photoresponse Properties of an n-ZnS/p-Si Heterojunction[J]. Chin. Phys. Lett., 2011, 28(12): 239-242
[11] ZHAO Chuan-Zhen**, LI Na-Na, WEI Tong, TANG Chun-Xiao . Temperature and Composition Dependence of GaNxAs1−x(0 < x ≤ 0.05) before and after Annealing[J]. Chin. Phys. Lett., 2011, 28(12): 239-242
[12] WANG Xiao, JIANG Zui-Min, XU Fei, **, MA Zhong-Quan, XU Run, YU Bin, LI Ming-Zhu, ZHENG Ling-Ling, FAN Yong-Liang, HUANG Jian, LU Fang . Enhancement of Er3+ Emission from an Er−Si Codoped Al2O3 Film by Stacking Si−Doped Al2O3 Sublayers[J]. Chin. Phys. Lett., 2011, 28(12): 239-242
[13] G. Murtaza, Iftikhar Ahmad, **, M. Maqbool, H. A. Rahnamaye Aliabad, A. Afaq . Structural and Optoelectronic Properties of Cubic CsPbF3 for Novel Applications[J]. Chin. Phys. Lett., 2011, 28(11): 239-242
[14] LIU Xing-Long, QIN Fu-Wen, **, BIAN Ji-Ming, ZHANG Dong, CHEN Wei-Ji, ZHOU Zhi-Feng, ZHI An-Bo, YU Bo, WU Ai-Min, JIANG Xin, . The Preparation and Characteristics of InxGa1−xN (0.06≤x≤0.58) Films Deposited by ECR-PEMOCVD[J]. Chin. Phys. Lett., 2011, 28(10): 239-242
[15] LU Yun-Qing, LI Pei-Li, ZHENG Jia-Jin. The Axial Spatial Evolution of Optical Field near the Talbot Plane of a Grating[J]. Chin. Phys. Lett., 2010, 27(9): 239-242
Viewed
Full text


Abstract