LI Run1, TANG Shi-Yu2, BAI Gang2, YIN Qiao-Nan2, LAN Xue-Xin1, XIA Yi-Dong2, YIN Jiang2**, LIU Zhi-Guo2 |
1National Laboratory of Solid State Microstructures and Department of Physics, Nanjing University, Nanjing 210093 2National Laboratory of Solid State Microstructures and Department of Materials Science and Engineering, Nanjing University, Nanjing 210093
|
|
Cite this article: |
LI Run, TANG Shi-Yu, BAI Gang et al 2013 Chin. Phys. Lett. 30 058101 |
|
|
Abstract GeTe4 films are deposited by using a dc magnetron sputtering technique, and its structural, thermal and electrical properties are investigated systematically. The prototypical phase-change memory cells are fabricated by using a focused ion beam and magnetron sputtering techniques. Compared with Ge2Sb2Te5, the GeTe4 film exhibits a higher crystallization temperature (235°C), better data retention of ten years at 129°C, and larger activation energy (2.94 eV). GeTe4 phase change memory cells with an effective diameter of 1 μm show proper switching speed, low power consumption, and good resistance contrast. The Set and Reset operations are achieved by using a 200-ns 2.0-V pulse and a 30-ns 3.0-V pulse, respectively. The dynamic switching ratio between the OFF and ON states is larger than 1×104.
|
|
Received: 30 January 2013
Published: 31 May 2013
|
|
PACS: |
81.07.-b
|
(Nanoscale materials and structures: fabrication and characterization)
|
|
85.35.-p
|
(Nanoelectronic devices)
|
|
68.60.Dv
|
(Thermal stability; thermal effects)
|
|
81.15.Cd
|
(Deposition by sputtering)
|
|
|
|
|
[1] Burr G W, Breitwisch M J, Franceschini M, Garetto D, Gopalakrishnan K and Jackson B et al 2010 J. Vac. Sci. Technol. B 28 2 [2] Atwood G 2008 Science 321 210 [3] Lankhorst M H R, Ketelaars B W S M M and Wolters R A M 2005 Nat. Mater. 4 347 [4] Wuttig M, Yamada N 2007 Nat. Mater. 6 824 [5] Lencer D, alinga M, Gravowski B, Hickel T, Neugebauer J and Wuttig M 2008 Nat. Mater. 7 972 [6] Wuttig M, Lüsebrink D, Wamwangi D, Welnic W, Gille M and Dronskowski R 2007 Nat. Mater. 6 122 [7] Kim Y, Jang M H, Jeong K, Cho M H, Do K H and Ko D H 2008 Appl. Phys. Lett. 92 061910 [8] Ryu S W, Oh J H, Lee J H, Choi B J and Kim W 2008 Appl. Phys. Lett. 92 142110 [9] Morales-Sanchez E, Lain B, Prokhorov E, Hernandez-Landaverde M A, Trapaga G and Gonzalez-Hernandez J 2010 Vacuum 84 877 [10] Lacaita A L and Wouters D J 2008 Phys. Status Solidi A 205 2281 [11] Jiang H, Guo K, Xu H N, Xia Y D, Jiang K, Tang F et al 2011 J. Appl. Phys. 109 066104 [12] Ren K, Rao F, Song Z T, Wu L C, Zhou X L, Xia M J et al 2010 Chin. Phys. Lett. 27 108101 [13] Yin Y, Sone H and Hosaka S 2007 J. Appl. Phys. 102 064503 [14] Li R, Guo Y H, Xu B, Su Y, Yin J, Zhang C H et al 2011 AIP Adv. 1 042115 [15] Park J W, Song M, Yoon S, Lim H Jeong D S, Cheong B, Lee H 2012 Phys. Status Solidi A 210 267 [16] Wang G X, Nie Q H, Shen X, Wang R P, Wu L C and Lv Y G 2012 Mater. Lett. 87 135 |
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|