Magnetism of a Nitrogen-Implanted TiO2 Single Crystal
LIU Chun-Ming1**, XIANG Xia1, ZHANG Yan2, JIANG Yong1, ZU Xiao-Tao1
1Department of Applied Physics, University of Electronic Science and Technology of China, Chengdu 610054 2School of Physics, Peking University, Beijing 100871
Magnetism of a Nitrogen-Implanted TiO2 Single Crystal
LIU Chun-Ming1**, XIANG Xia1, ZHANG Yan2, JIANG Yong1, ZU Xiao-Tao1
1Department of Applied Physics, University of Electronic Science and Technology of China, Chengdu 610054 2School of Physics, Peking University, Beijing 100871
摘要Single rutile crystal TiO2 was implanted using nitrogen ions with energy of 60 keV. The microstructure, ultraviolet−visible light absorption spectra, conductivity and magnetism are investigated. Except for the nitrogen dopant, no impurity can be detected by x-ray diffraction and x-ray photoelectron spectra. The absorption in the visible light region is enhanced with nitrogen implantation dose increasing. By measuring the temperature dependence of resistance, it is found that the sample implanted with 1×1018 ions/cm2 is changes from insulating to semiconducting, and the variable range hopping is the main conducting mechanism. Room-temperature ferromagnetism is also obtained in this sample. The magnetism as a function of temperature can be well fitted using the three-dimensional spin wave model plus the Curie–Weiss model, indicating that there is a mixed phase of ferromagnetism and paramagnetism.
Abstract：Single rutile crystal TiO2 was implanted using nitrogen ions with energy of 60 keV. The microstructure, ultraviolet−visible light absorption spectra, conductivity and magnetism are investigated. Except for the nitrogen dopant, no impurity can be detected by x-ray diffraction and x-ray photoelectron spectra. The absorption in the visible light region is enhanced with nitrogen implantation dose increasing. By measuring the temperature dependence of resistance, it is found that the sample implanted with 1×1018 ions/cm2 is changes from insulating to semiconducting, and the variable range hopping is the main conducting mechanism. Room-temperature ferromagnetism is also obtained in this sample. The magnetism as a function of temperature can be well fitted using the three-dimensional spin wave model plus the Curie–Weiss model, indicating that there is a mixed phase of ferromagnetism and paramagnetism.
(Optical properties of bulk materials and thin films)
引用本文:
LIU Chun-Ming**;XIANG Xia;ZHANG Yan;JIANG Yong;ZU Xiao-Tao
. Magnetism of a Nitrogen-Implanted TiO2 Single Crystal[J]. 中国物理快报, 2011, 28(12): 127201-127201.
LIU Chun-Ming**, XIANG Xia, ZHANG Yan, JIANG Yong, ZU Xiao-Tao
. Magnetism of a Nitrogen-Implanted TiO2 Single Crystal. Chin. Phys. Lett., 2011, 28(12): 127201-127201.
[1] Kim J Y et al 2003 Phys. Rev. Lett. 90 017401
[2] Yoon S D et al 2006 J. Phys: Condens. Matter 18 L355
[3] Zhou S et al 2009 Phys. Rev. B 79 113201
[4] Cruz M M et al 2009 J. Phys. : Condens. Matter 21 206002
[5] Tao J G et al 2009 Appl. Phys. Lett. 95 062505
[6] Li Q K et al 2007 Phys. Status Solidi 1 217
[7] Yang K et al 2010 Phys. Rev. B 81 033202
[8] Keys L K and Mulay L N 1967 Phys. Rev. 154 453
[9] Sawai Y, Hazu K and Chichibu S F 2010 J. Appl. Phys. 108 063541
[10] Lai Y K et al 2010 J. Hazardous Mater. 184 855
[11] Chen S Z et al 2004 Catal. Commun. 5 677
[12] Diwald O et al 2004 J. Phys. Chem. B 108 6004
[13] Mahalingam S and Edirisinghe M J 2008 J. Phys. D: Appl. Phys. 41 215406
[14] Liu C M et al 2008 Can. J. Phys. 86 1345
[15] Nakano Y et al 2005 Appl. Phys. Lett. 87 052111
[16] Lee J Y et al 2005 Appl. Phys. Lett. 87 011904
[17] Majumdar S and Banerji P 2010 J. Appl. Phys. 107 063702
[18] Huang J C A et al 2004 Appl. Phys. Lett. 85 3815
[19] Yang K et al 2008 Appl. Phys. Lett. 93 132507
[20] Borges R P et al 2007 J. Phys. : Condens. Matter 19 476207
[21] Kim D H et al 2003 Appl. Phys. Lett. 83 4574
[22] Drera G et al 2010 Appl. Phys. Lett. 97 012506
[23] Bao N N et al 2011 J. Appl. Phys. 109 07C302
2011, Vol. 28 