Abstract：One-dimensional (1D) transition metal phosphides (TMPs) with large specific surface areas, high charge transfer efficiency and excellent electrical conductivity have attracted significant attention in hydrogen evolution reaction (HER) as versatile and active catalysts. Herein, the sub-4 nm Mo-Co$_{2}$P ultrafine nanorods (NRs) anchored on reduced graphene oxide (rGO) were successfully synthesized by a colloidal mesostructured strategy. Electrochemical test results reveal that the Mo-Co$_{2}$P@rGO electrode exhibits superior activity with overpotentials of 204 mV and Tafel slope of 88 mV/dec for HER at 10 mA/cm$^{2}$, relative to the Co$_{2}$P@rGO electrode in 0.5 M H$_{2}$SO$_{4}$ solution. This improvement could be ascribed to the Mo doping, which results in more active sites, higher electrical conductivity and faster electron-transfer rates. This versatile strategy will provide a promising pathway for transition metal-doped compounds as an efficient catalyst.
Yang X L, Lu A Y, Zhu Y H, Hedhili M N, Min S X, Huang K W, Han Y and Li L J 2015 Nano Energy15 634
[27]
Zhang L L, Yan S, Jiang S, Yang K, Wang H, He S M, Liang D X, Zhang L, He Y, Lan X Y, Mao C W, Wang J, Jiang H, Zheng Y, Dong Z H, Zeng L Y and Li A G 2015 Nucl. Sci. Tech.26 060101
Pan Y, Sun K A, Lin Y, Cao X, Cheng Y S, Liu S J, Zeng L Y, Cheong W C, Zhao D, Wu K L, Liu Z, Liu Y Q, Wang D S, Peng Q, Chen C and Li Y D 2019 Nano Energy56 411
2020, Vol. 37 