Influence of Zn Ions Codoping on Luminescence Properties of PbWO4:RE(RE=La, Yb, Y) |
XU Yan-Ling1;WANG Rui1;WANG Bin-Ju1,2;LIU Wei-Hai1;WANG Jia1;WANG Miao1;YANG Tong-Yong1 |
1Department of Applied Chemistry, Harbin Institute of Technology, Harbin 1500012State Key Laboratory for Physical Chemistry of Solid Surfaces, Department of Chemistry, Institute of Physical Chemistry, Xiamen University, Xiamen 361005 |
|
Cite this article: |
XU Yan-Ling, WANG Rui, WANG Bin-Ju et al 2008 Chin. Phys. Lett. 25 2246-2248 |
|
|
Abstract Zn and RE (RE=La, Yb, Y) ions co-doped PbWO4 (PWO) single crystal grown by the Czochralski technique are characterized by x-ray diffraction (XRD), optical transmission spectra, and photoluminescence (PL). The doping of Zn ions shows distinct effects on the properties of PWO:RE crystals. At low concentration of Zn ions (200ppm), the luminescence intensity is quite weak for (Zn,La)-doped PWO, but is substantially strong for (Zn,Yb)-doped PWO. The blue luminescence intensity is significantly enhanced with the increasing Zn ions doping for PWO:Y. The trivalent ions codoping can increase the ratio of the blue luminescence contributing to the fast components of light yield. Yb ions can enhance efficiency of luminescence in PWO:Yb:Zn because they may act as a luminous sensitization agent which can be involved in the efficient energy transfer and storage of the radiative process.
|
Keywords:
76.30.Kg
61.72.Ji
61.72.Ww
|
|
Received: 19 January 2008
Published: 31 May 2008
|
|
|
|
|
|
[1] Nikl M 2000 Phys. Status Solidi A 178 595 [2] Auffray E, Davies G, Lecoq P, Marcos R, Sempere P,Schneegans M, Annenkov A and Korzhik M 2000 Nucl. Instrum.Methods Phys. Res. A 453 218 [3] Han B G, Feng X Q, Hu G Q, Wang P C and Yin Z W 1998 J. Appl. Phys 84 2831 [4] Li W S, Tang T B, Huang H W and Feng X Q 2001 J.Appl. Phys 40 6893 [5] Huang Y L et al 2003 Mater. Lett. 58 159 [6] Kobayashi M et al 1997 Nucl. Instrum. Methods Phys.Res. A 399 26 [7] Zhang X et al 2004 Chem. Phys. Lett. 383 245 [8] Kobayashi M, Usuki Y, Ishii M, Itoh M and Nikl M 2005 Nucl. Instrum. Methods Phys. Res. A 540 381 [9] Annenkov A, Auffray E, Korzhi M and Lecoq P 1998 Phys. Status Solidi A 170 47 [10] Liu T Y et al 2005 Solid State Commun. 135382 [11] Zhang X Y, Zhang Q R, Chen T and Liu T Y 2006 J.University of Shanghai for Science and Technology 28 6 (inChinese) [12] Chen T and Liu T Y et al 2006 Chin. Phys. Lett 23 3323 [13] Chen T. and Liu T Y et al 2007 Phys. Lett. A 363 477 [14] Annenkov A N, Auffray E and Borisevich A E et al 2002 Phys. Status Solidi A 19 277 [15] Zorenko Y, Voloshinovskii A and Moroz Z 2004 Radiat.Measure 38 397 [16] Van Loo W 1979 Phys. Status Solidi A 27 565 |
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|