MARTENSITIC TRANSFORMATION, THERMOMAGNETIC PROPERTIES AND ELECTRONIC RESISTIVITY OF AMORPHOUS ALLOYS (Fe1-xNix)84B16 AFTER CRYSTALLIZATION |
GUO Huiqun;ZHAO Jiangao;SHEN Baogen;ZHAN Wenshan;LI Xiaogang;YANG Linyuan |
Institute of Physics, Academia Sinica, Beijing |
|
Cite this article: |
GUO Huiqun, ZHAO Jiangao, SHEN Baogen et al 1988 Chin. Phys. Lett. 5 553-556 |
|
|
Abstract In the reduced curves of electronic resistivity and thermomagnetic measurement of the amorphous alloys, (Fe1-xNix)84B16 with 0.02< x <0.08, preheated to a temperature higher than that of crystallization, an anomalous abruption at about 150°C was observed. The results of differential thermal analysis (DTA) and of X-ray diffraction show that after crystallization of the amorphous alloys (Fe1-xNix)84B16 the anomalous abruption can be attributed to the martensitic transformation of γFe(Ni) to αFe(Ni).
|