Surface Free Energies and Morphologies of Chemical Vapor Deposited Diamond Films
ZHANG Yafei, ZHANG Fangqing, CHEN Guanghua
Department of Physics, Lanzhou University, Lanzhou 730001
Surface Free Energies and Morphologies of Chemical Vapor Deposited Diamond Films
ZHANG Yafei;ZHANG Fangqing;CHEN Guanghua
Department of Physics, Lanzhou University, Lanzhou 730001
关键词 :
68.55.+b ,
82.65.-i ,
68.40.+e
Abstract : We have calculated the surface free energies of the chemical vapor deposited diamond crystals during the preparation process, using the model that a fraction of carbon dangling bonds on the growth surface are saturated by hydrogen. The results show that the surface free energies of the three most energetically favored crystal planes, i. e. (100), (110) and (111), can be used to interpret the changes of predominant facets in the surface morphology from {100} to {111} with increasing substrate temperature. In chemical vapor deposition conditions, it is found that the growth surfaces of diamond are more stable than that of graphite.
Key words :
68.55.+b
82.65.-i
68.40.+e
出版日期: 1994-08-01
引用本文:
ZHANG Yafei;ZHANG Fangqing;CHEN Guanghua. Surface Free Energies and Morphologies of Chemical Vapor Deposited Diamond Films[J]. 中国物理快报, 1994, 11(8): 502-505.
ZHANG Yafei, ZHANG Fangqing, CHEN Guanghua. Surface Free Energies and Morphologies of Chemical Vapor Deposited Diamond Films. Chin. Phys. Lett., 1994, 11(8): 502-505.
链接本文:
https://cpl.iphy.ac.cn/CN/
或
https://cpl.iphy.ac.cn/CN/Y1994/V11/I8/502
[1]
GUO Deng-Zhu;HOU Shi-Min;SHEN Zi-Yong; ZHAO Xing-Yu;LIU Wei-Min;XUE Zeng-Quan. Preparation and Annealing-Induced Structural Transition of Self-Organized Nanostripes on the Electropolished Aluminum Surface [J]. 中国物理快报, 2002, 19(3): 385-388.
[2]
ZHU Jun;MA Li;WANG Shao-Jie;LUO Xi-Hui. Reaction of Positronium with Proton in Ultra-stable Y Zeolite Studied by Positrons [J]. 中国物理快报, 2000, 17(2): 134-136.
[3]
WU Jian-xin;MA Mao-sheng;LIU Xian-ming. Ultraviolet Photoelectron Spectroscopy Study of Oxygen Adsorption on Rb-Covered InSb (111) Surfaces [J]. 中国物理快报, 1998, 15(8): 605-607.
[4]
LIANG Qi;WU Jian-xin;JI Ming-rong;MA Mao-sheng;LIU Xian-ming;ZHANG Yu-heng. Photoemission of the Oxidation of Cerium Overlayers on GaSb(110) Surface [J]. 中国物理快报, 1997, 14(10): 793-797.
[5]
XIE Jianjun;JIANG Ping;ZHANG Kaiming. Theoretical Studies on Vibrationally Assisted Adsorption of
H2 on Cu(100) Surface
[J]. 中国物理快报, 1995, 12(10): 637-640.
[6]
GU Hongen;CHEN Zhifang;LI Zhijuan. Spectral Property and Stability of Color Centers in Alkali Halide Crystals Induced by He+ Ion Implantation at Room Temperature [J]. 中国物理快报, 1993, 10(3): 163-166.
[7]
CHEN Zhiquan;WANG Shaojie (S. J. Wang). Observation of Spin-Conversion of Positronium in Zeolite [J]. 中国物理快报, 1993, 10(11): 684-687.
[8]
GUO shuwen;TAN shongsheng;WANG Weiyuan;. PREPARATION AND CHARACTERIZATION OF HEAVILY DOPED μc-Si:F:H FILMS BY WINDOWLESS PHOTO-CVD [J]. 中国物理快报, 1989, 6(12): 563-565.