Pyroelectricity and Spontaneous Polarization in [111] Oriented 0.955Pb(Zn1/3Nb2/3)O3--0.045PbTiO3 Single Crystals
SHEN Ming-Rong1, YAO Dong-Lai1, CAO Wen-Wu2
1Department of Physics, Suzhou University, Suzhou 215006
2Department of Mathematics and Materials Research Institute, The Pennsylvania State University, University Park, PA 16802, USA
Pyroelectricity and Spontaneous Polarization in [111] Oriented 0.955Pb(Zn1/3Nb2/3)O3--0.045PbTiO3 Single Crystals
SHEN Ming-Rong1;YAO Dong-Lai1;CAO Wen-Wu2
1Department of Physics, Suzhou University, Suzhou 215006
2Department of Mathematics and Materials Research Institute, The Pennsylvania State University, University Park, PA 16802, USA
Abstract: We report that the measurements of the pyroelectric current of the pre-poled [111]-oriented 0.955Pb(Zn1/3Nb2/3)O3--0.045PbTiO3 (PZN-4.5%PT) single crystals can shed some light on the phase transition and spontaneous polarization characters of this material in a similar way to measures of remanent polarization and dielectric properties. The pyroelectric current is measured and the corresponding spontaneous polarization is calculated as a function of temperature with various poling fields added during cooling the sample from 200°C to room temperature. Critical electric field of 0.061kV/cm is found to be essential to induce the intermediate ferroelectric orthorhombic phase between the ferroelectric rhombohedral and tetragonal phases. Below the critical field, the polarization increases almost linearly with the increase of poling field. At the critical field, the polarization at 30°C increases abruptly from 14μC/cm2 for a poling field of 0.06kV/cm to 29.5μC/cm2 for a poling field of 0.061kV/cm, and afterwards, increases slowly and saturates to 31muC/cm2 for poling fields beyond 0.55kV/cm.