Spall in Aluminium with Helium Bubbles under Laser Shock Loading
Da-Wu Xiao1** , Li-Feng He1 , Ping Zhou1 , Dong-Li Zou1 , Hua Shu2
1 Institute of Materials, China Academy of Engineering Physics, Mianyang 6217002 Institute of Laser, China Academy of Engineering Physics, Mianyang 621700
Abstract :The spallation behaviors of Al+0.2 wt% $^{10}$B targets and neutron irradiated Al+0.2 wt% $^{10}$B targets with 5 nm radius helium bubble subjected to direct laser ablation are presented. It is found that the spall strength increases significantly with the tensile strain rate, and the helium bubble or boron inclusions in aluminum reduces the spall strength of materials by 34%. However, slight difference is observed in the spall strength of unirradiated samples compared with the irradiated sample with helium bubbles.
收稿日期: 2016-12-02
出版日期: 2017-04-29
:
62.50.-p
(High-pressure effects in solids and liquids)
62.50.Ef
(Shock wave effects in solids and liquids)
62.20.mm
(Fracture)
[1] Chen X, Asay J R, Dwivedi S K and Field D P 2006 J. Appl. Phys. 99 023528 [2] Wang Y, He H, Qi M, Shen L and Bai B 2007 J. Appl. Phys. 102 073518 [3] Wang Y, Qi M, He H and Wang L 2014 Mech. Mater. 69 270 [4] Satou M, Koide H, Hasegawa A, Abe K, Kayano H and Matsui H 1996 J. Nucl. Mater. 233 447 [5] Moreno D and Eliezer D 1996 Scrip. Mater. 35 1385 [6] Marian J, Wirth B D and Perlado M 2002 Phys. Rev. Lett. 88 255507 [7] Kubota A, Reisman D B and Wolfer W G 2006 Appl. Phys. Lett. 88 241924 [8] Shao J L, Wang P and He A M 2014 J. Appl. Phys. 116 111 [9] Raicher E, Glam B, Henis Z, Pecker S, Eliezer S and Moreno D 2009 J. Appl. Phys. 106 083519 [10] Glam B, Eliezer S, Moreno D and Eliezer D 2009 J. Nucl. Mater. 392 413 [11] Glam B, Eliezer S, Moreno D, Eliezer D, Perelmutter L, Sudai M and Eliezer D 2010 Int. J. Fract. 163 217 [12] Glam B, Strauss M, Eliezer D and Moreno D 2014 Int. J. Impt. Eng. 65 1 [13] Kanel G I, Razorenov S V, Baumung K and Singer J 2001 J. Appl. Phys. 90 136 [14] Kanel G I, Razorenov S V, Bogatch A A and Grady D E 1996 J. Appl. Phys. 79 8310 [15] Qi M L, Zhong S, He H L, Fan D and Zhao L 2013 Chin. Phys. B 22 046203 [16] Trivedi P E, Asay J R, Gupta Y M and Field D P 2007 J. Appl. Phys. 102 083513
[1]
. [J]. 中国物理快报, 2023, 40(3): 37403-.
[2]
. [J]. 中国物理快报, 2023, 40(1): 17403-.
[3]
. [J]. 中国物理快报, 2022, 39(9): 96201-.
[4]
. [J]. 中国物理快报, 2022, 39(5): 56101-.
[5]
. [J]. 中国物理快报, 2021, 38(6): 66201-.
[6]
. [J]. 中国物理快报, 2021, 38(3): 36201-.
[7]
. [J]. 中国物理快报, 2020, 37(10): 107401-.
[8]
. [J]. 中国物理快报, 2020, 37(8): 80701-.
[9]
. [J]. 中国物理快报, 2020, 37(7): 76201-.
[10]
. [J]. 中国物理快报, 2020, 37(7): 76202-.
[11]
. [J]. 中国物理快报, 2020, 37(7): 76203-.
[12]
. [J]. 中国物理快报, 2020, 37(6): 66201-.
[13]
. [J]. 中国物理快报, 2020, 37(6): 66202-.
[14]
. [J]. 中国物理快报, 0, (): 66201-.
[15]
. [J]. 中国物理快报, 2020, 37(4): 44204-.