Optical Limiting Properties of Ag-Cu Metal Alloy Nanoparticles Analysis by using MATLAB
WANG Yu-Hua1**, LI Hui-Qing2, LU Jian-Duo1, WANG Ru-Wu1
1Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, and Department of Applied Physics, Wuhan University of Science and Technology, Wuhan 430081 2Department of Endocrinology, Union Hospital, Tongji Medical College, Huazhong University of Science and Technology, Wuhan 430022
Optical Limiting Properties of Ag-Cu Metal Alloy Nanoparticles Analysis by using MATLAB
WANG Yu-Hua1**, LI Hui-Qing2, LU Jian-Duo1, WANG Ru-Wu1
1Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, and Department of Applied Physics, Wuhan University of Science and Technology, Wuhan 430081 2Department of Endocrinology, Union Hospital, Tongji Medical College, Huazhong University of Science and Technology, Wuhan 430022
摘要Ag-Cu alloy nanoparticles were formed by sequential ion implantation (Ag and Cu) in silica using a metal vapor vacuum arc (MEVVA) ion source. Third-order nonlinear optical properties of the nanoparticles were measured at 1064 nm excitations using the Z-scan technique. Curve fitting analysis, based on the MATLAB features for Ag-Cu alloy nanoparticle optical limiting experiments, is used. The results show that Ag-Cu alloy nanoparticles display a refractive optical limiting effect at 1064 nm.
Abstract：Ag-Cu alloy nanoparticles were formed by sequential ion implantation (Ag and Cu) in silica using a metal vapor vacuum arc (MEVVA) ion source. Third-order nonlinear optical properties of the nanoparticles were measured at 1064 nm excitations using the Z-scan technique. Curve fitting analysis, based on the MATLAB features for Ag-Cu alloy nanoparticle optical limiting experiments, is used. The results show that Ag-Cu alloy nanoparticles display a refractive optical limiting effect at 1064 nm.
WANG Yu-Hua**;LI Hui-Qing;LU Jian-Duo;WANG Ru-Wu
. Optical Limiting Properties of Ag-Cu Metal Alloy Nanoparticles Analysis by using MATLAB[J]. 中国物理快报, 2011, 28(11): 116101-116101.
WANG Yu-Hua**, LI Hui-Qing, LU Jian-Duo, WANG Ru-Wu
. Optical Limiting Properties of Ag-Cu Metal Alloy Nanoparticles Analysis by using MATLAB. Chin. Phys. Lett., 2011, 28(11): 116101-116101.
[1] Stepanov A L 2011 Rev. Adv. Mater. Sci. 27 115
[2] Battaglin G, Calvelli P, Cattaruzza E, Gonella F, Polloni R, Mattei G and Mazzoldi P 2001 Appl. Phys. Lett. 78 3953
[3] Falconieri M, Salvetti G, Cattaruzza E, Gonella F, Mattei G, Mazzoldi P, Piovesan M, Battaglin G and Polloni R 1998 Appl. Phys. Lett. 73 288
[4] Wang Y H, Ren F, Wang Q Q, Chen D J, Fu D J and Jiang C Z 2006 Phys. Lett. A 357 364
[5] Haglund R F, Jr, Yang L, Magruder R H, Wittig J E, Becker K and Zuhr R A 1993 Opt. Lett. 18 373
[6] Wang Y H, Wang Y M, Lu J D, Ji L L, Zhang R G and Wang R W 2010 Opt. Commun. 283 486
[7] Wang Y H, Wang Y M, Lu J D, Ji L L, Zhang R G and Wang R W 2009 Physica B 404 4295
[8] Wang Y H, Jiang C Z, Ren F, Wang Q Q, Chen D J and Fu D J 2006 Phys. E 33 244
[9] Ganeev R A, Ryasnyansky A I, Kamalov S R, Kodirov M K and Usmanov T 2001 J. Phys. D: Appl. Phys. 34 1602
[10] Ryasnyanskiy A I, Palpant B, Debrus S, Pal U and Stepanov A L 2007 Opt. Commun. 273 538
[11] Francois L, Mostafavi M and Belloni J 2000 J. Phys. Chem. B 104 6133
[12] Wang Y H, Wang Y M, Han C J, Lu J D, Ji L L and Wang R W 2010 Vacuum 85 207
[13] Wang Y H, Wang Y M, Han C J, Lu J D, Ji L L and Wang R W 2010 Physica B 405 2848
[14] Wang Y H, Jiang C Z, Ren F, Wang Q Q, Chen D J and Fu D J 2007 J. Mater. Sci. 42 7294
[15] Gonella F, Mattei G, Mazzoldi P and Sada C 1999 Appl. Phys. Lett. 75 55
[16] Sheik-Bahae M, Said A A, Wei T H, Hagan D J and Van Stryland E W 1990 IEEE J. Quantum Electron. 26 760
[17] Sheik-Bahae M, Hagan D J and Van Stryland E W 1990 Phys. Rev. Lett. 65 96
2011, Vol. 28 