Ne2+ Ion Irradiation Induced Swelling Effects in Pyrochlore Ho2Ti2O7 by Using a GIXRD Technique
LI Yu-Hong1,2**, XU Chun-Ping1, GAO Chao1, WANG Zhi-Guang2
1School of Nuclear Science and Technology, Lanzhou University, Lanzhou 730000 2Institute of Modern Physics, Chinese Academy of Sciences, Lanzhou 730000
Ne2+ Ion Irradiation Induced Swelling Effects in Pyrochlore Ho2Ti2O7 by Using a GIXRD Technique
LI Yu-Hong1,2**, XU Chun-Ping1, GAO Chao1, WANG Zhi-Guang2
1School of Nuclear Science and Technology, Lanzhou University, Lanzhou 730000 2Institute of Modern Physics, Chinese Academy of Sciences, Lanzhou 730000
摘要We carry out 400 keV Ne2+ ion irradiation damage experiments at cryogenic temperature (about 77 K) on polycrystalline Ho2Ti2O7 pyrochlore. The irradiation fluences range from 2×1014 to 1.3×1015 ions/cm2, corresponding to the peak ballistic displacement damage of 0.075–0.487 in units of displacement per atom (dpa). The value indicates the statistical average of the fractional number of lattice atoms which have experienced a lattice displacement. Irradiation−induced structural evolution is examined by using grazing incidence x-ray diffraction (GIXRD) at x-ray angles γ=0.25° and 3°. It is found that the irradiated layer is volumetrically swelled as compared with the underlying non-irradiated substrate and the volume increase in the irradiated layer is contributed mainly to the irradiated ion fluence.
Abstract：We carry out 400 keV Ne2+ ion irradiation damage experiments at cryogenic temperature (about 77 K) on polycrystalline Ho2Ti2O7 pyrochlore. The irradiation fluences range from 2×1014 to 1.3×1015 ions/cm2, corresponding to the peak ballistic displacement damage of 0.075–0.487 in units of displacement per atom (dpa). The value indicates the statistical average of the fractional number of lattice atoms which have experienced a lattice displacement. Irradiation−induced structural evolution is examined by using grazing incidence x-ray diffraction (GIXRD) at x-ray angles γ=0.25° and 3°. It is found that the irradiated layer is volumetrically swelled as compared with the underlying non-irradiated substrate and the volume increase in the irradiated layer is contributed mainly to the irradiated ion fluence.
LI Yu-Hong;**;XU Chun-Ping;GAO Chao;WANG Zhi-Guang
. Ne2+ Ion Irradiation Induced Swelling Effects in Pyrochlore Ho2Ti2O7 by Using a GIXRD Technique[J]. 中国物理快报, 2011, 28(6): 66102-066102.
LI Yu-Hong, **, XU Chun-Ping, GAO Chao, WANG Zhi-Guang
. Ne2+ Ion Irradiation Induced Swelling Effects in Pyrochlore Ho2Ti2O7 by Using a GIXRD Technique. Chin. Phys. Lett., 2011, 28(6): 66102-066102.
[1] Beaury M, Dalmasso C, Thiriet-Dodane C, Simeone D and Gosset D 2006 Nucl. Instrum. Methods B 242 557
[2] Ewing R C, Weber W J and Lian J 2004 J. Appl. Phys. 95 5949
[3] Weber W J, Ewing R C, Catlow C R A, Diaz de la Rubia T, Hobbs L W, Kinoshita C, Matzke H, Motta A T, Nastasi M, Salje E H K, Vance E R and Zinkle S J 1998 J. Mater. Res. 13 1434
[4] Weber W J, Navrotsky A, Stefanovsky S, Vance E R and Vernaz E 2009 MRS Bull 34 46
[5] Sickafus K E, Minervini L, Grimes R W, Valdez J A, Ishimaru M, Lim F McClellan K J and Hartmann T 2000 Science 289 748
[6] Sickafus K E, Grimes R W, Valedz J A, Cleave A, Tang M Iishimaru M, Corish S M, Steanke C R and Uberuaga B P 2007 Nature Mater 6 217
[7] Lian J, Wang L, Chen J, Sun K, Ewing R C, Farmer J M and Boatner L A 2003 Acta Materialia 51 1493
[8] Lian J, Chen J Wang L M, Ewing R C, Farmer J M, Boatner L A and Helean K B 2003 Phys. Rev. B 68 134107
[9] Wang S X, Wang L M, Ewing R C and Govindan Kutty K V 2000 Nucl. Instrum. Methods B 169 135
[10] Lian J, Wang L M, Ewing R C and Boatner L A 2005 Nucl. Instrum. Methods B 241 365
[11] Lian J, Wang L M, Ewing R C and Boatner L A 2006 Nucl. Instrum. Methods B 242 448
[12] Ziegler J F, Biersack J P and Littmark U 1996 The Stopping and Range of Ions in Matter (SRIM) www.srim.org
[13] Guiner A 1994 X-Ray Diffraction in Crystals, Imperfect Crystal and Amorphous BODIES (New York: Dover)
[14] Lim G, Parrish W, Ortiz C, Bellotto M and Hart M 1987 J. Mater. Res. 2 471
[15] Murakami T, Chakoumakos B C, Ewing R C, Lumpkin G R and Weber W J 1991 Am. Mineral. 76 1510
[16] Patel M K, Vijayakumar V, Avasthi D K, Kailas S, Pivin J C, Grover V, Mandal B P and Tyagi A K 2008 Nucl. Instrum. Methods B 266 2898
[17] Patel M K, Vijayakumar V, Kailas S, Avasthi D K, Pivin J C and Tyagi A K 2008 J. Nucl. Mater. 380 93
2011, Vol. 28 