Fragile-to-Strong Transition in Al-Ni-M (M=La, Pr, Nd) Metallic Glasses
ZHANG Chun-Zhi1, HU Li-Na1**, BIAN Xiu-Fang1, YUE Yuan-Zheng1,2
1Key Laboratory of Liquid Structure and Heredity of Materials (Ministry of Education), Shandong University, Jinan 250061 2Section of Chemistry, Aalborg University, DK-9000 Aalborg, Denmark
Fragile-to-Strong Transition in Al-Ni-M (M=La, Pr, Nd) Metallic Glasses
ZHANG Chun-Zhi1, HU Li-Na1**, BIAN Xiu-Fang1, YUE Yuan-Zheng1,2
1Key Laboratory of Liquid Structure and Heredity of Materials (Ministry of Education), Shandong University, Jinan 250061 2Section of Chemistry, Aalborg University, DK-9000 Aalborg, Denmark
摘要We study the dynamic behavior of marginal metallic glass-forming liquids Al-Ni-M (M=La, Pr, Nd) in terms of liquid fragility in high and low temperature regions. The liquids are extremely fragile above the liquidus temperature T liq, but become rather strong near the glass transition temperature Tg. The strength of the transition is inversely correlated with the fragility index at Tg. This relation is discussed in terms of potential energy landscape.
Abstract:We study the dynamic behavior of marginal metallic glass-forming liquids Al-Ni-M (M=La, Pr, Nd) in terms of liquid fragility in high and low temperature regions. The liquids are extremely fragile above the liquidus temperature T liq, but become rather strong near the glass transition temperature Tg. The strength of the transition is inversely correlated with the fragility index at Tg. This relation is discussed in terms of potential energy landscape.
[1] Angell C A 1995 Science 267 1924
[2] Hu L N et al 2004 Acta Mater. 52 4773
[3] Angell C A 1988 J. Non-Cryst. Solids 102 205
[4] Debenedetti P G and Stillinger F H 2001 Nature 410 259
[5] Hu L N et al 2005 J. Phys. Chem. B 109 13737
[6] Ngai K L 1998 Phys. Rev. E 57 7346
[7] Rössler E, Hess K-U, Novikov V N 1988 J. Non-Cryst. Solids 223 207
[8] Ito K, Moynihan C T and Angell C A 1999 Nature 398 492
[9] Barrat J L, Badro J and Gillet P 1997 Mol. Simul. 20 17
[10] Hemmati M, Moynihan C T and Angell C A 2001 J. Chem. Phys. 115 6663
[11] Way C, Wadhwa P and Busch R, 2007 Acta Mater. 55 2977
[12] Wang D et al 2010 Chin. Phys. Lett. 27 036401
[13] Zhang C Z et al 2010 J. Chem. Phys. 133 014508
[14] Mauro J C et al 2009 Natl. Acad. Sci. USA 106 19780
[15] Steinberg J, Tyagi S and Lord Jr A E 1981 Acta Metall. 29 1309
[16] Lu Z P, Li Y and Liu C T 2003 J. Appl. Phys. 93 286
[17] Yue Y Z, Ohe R von der and Jensen S L 2004 J. Chem. Phys. 120 8053
Yue Y Z, Ohe R von der and Jensen S L 2004 J. Chem. Phys. 121 11508
[18] Bian X F et al 2005 Phys. Lett . A 335 61
[19] Angelani L et al 1998 Phys. Rev. Lett. 81 4648
[20] Angelani L et al 2000 Phys. Rev. Lett. 85 5356
[21] Scopigno T et al 2003 Science 302 849