Reply to “Comment on ‘High Mixing Entropy Enhanced Energy States in Metallic Glasses’”
Juntao Huo1 , Kangyuan Li2 , Bowen Zang1 , Meng Gao1 , Li-Min Wang3 , Baoan Sun4 , Maozhi Li2* , Lijian Song1* , Jun-Qiang Wang1* , and Wei-Hua Wang4
1 CAS Key Laboratory of Magnetic Materials and Devices, and Zhejiang Province Key Laboratory of Magnetic Materials and Application Technology, Ningbo Institute of Materials Technology & Engineering, Chinese Academy of Sciences, Ningbo 315201, China2 Department of Physics, Renmin University of China, Beijing 100872, China3 State Key Lab of Metastable Materials Science and Technology, and College of Materials Science and Engineering, Yanshan University, Qinhuangdao 066004, China4 Institute of Physics, Chinese Academy of Sciences, Beijing 100190, China
收稿日期: 2022-07-19
出版日期: 2022-10-24
:
64.70.pe
(Metallic glasses)
65.60.+a
(Thermal properties of amorphous solids and glasses: heat capacity, thermal expansion, etc.)
引用本文:
. [J]. 中国物理快报, 2022, 39(11): 119902-.
链接本文:
https://cpl.iphy.ac.cn/CN/10.1088/0256-307X/39/11/119902
或
https://cpl.iphy.ac.cn/CN/Y2022/V39/I11/119902
[1] Li M X, Zhao S F, Lu Z, Hirata A, Wen P, Bai H Y, Chen M, Schroers J, Liu Y, and Wang W H 2019 Nature 569 99 [2] Li Y, Guo Q, Kalb J A, and Thompson C V 2008 Science 322 1816 [3] Jilani S, Koloadin L S, Miskovic D M, and Laws K J 2021 Scr. Mater. 204 114120 [4] Ristić R, Figueroa I A, Salčinović F A, Zadro K, Mikšić T V, Pervan P, and Babić E 2021 J. Appl. Phys. 130 195102 [5] Wang F, Inoue A, Han Y, Zhu S L, Kong F L, Zanaeva E, Liu G D, Shalaan E, Al-Marzouki F, and Obaid A 2017 J. Alloys Compd. 723 376 [6] Huo J T, Li K Y, Zang B W, Gao M, Wang L M, Sun B A, Li M Z, Song L J, Wang J Q, and Wang W H 2022 Chin. Phys. Lett. 39 046401 [7] Ding H Y, Shao Y, Gong P, Li J F, and Yao K F 2014 Mater. Lett. 125 151 [8] Zhao S F, Shao Y, Liu X, Chen N, Ding H Y, and Yao K F 2015 Mater. & Des. 87 625 [9] Takeuchi A, Chen N, Wada T, Yokoyama Y, Kato H, Inoue A, and Yeh J W 2011 Intermetallics 19 1546 [10] Kohda M, Haruyama O, Ohkubo T, and Egami T 2010 Phys. Rev. B 81 092203
[1]
.
[2]
.
[3]
.
[4]
.
[5]
.
[6]
.
[7]
.
[8]
KE Hai-Bo,ZHAO Zuo-Feng,WEN Ping**,WANG Wei-Hua. Specific Heat in a Typical Metallic Glass Former
[9]
ZHANG Chun-Zhi;HU Li-Na**;BIAN Xiu-Fang;YUE Yuan-Zheng;
. Fragile-to-Strong Transition in Al-Ni-M (M=La, Pr, Nd) Metallic Glasses
[10]
ZHUO Long-Chao;PANG Shu-Jie;WANG Hui;ZHANG Tao. Ductile Bulk Aluminum-Based Alloy with Good Glass-Forming Ability and High Strength
[11]
JIANG Min-Qiang;JIANG Si-Yue$;DAI Lan-Hong;. Inherent Shear-Dilatation Coexistence in Metallic Glass
[12]
YANG Hong-Wang;TONG Wei-Ping;ZHAO Xiang;ZUO Liang;WANG Jian-Qiang. Observation of β-Relaxation in Sub-Tg Isothermally Annealed Al-Based Metallic Glasses
[13]
GUO Xiao-Lin;SHAN De-Bin;MA Ming-Zhen;GUO Bin. Compressive Deformation Induced Nanocrystallization of a Supercooled Zr-Based Bulk Metallic Glass
2022, Vol. 39 