A New Cu-Based Metallic Glass Composite with Excellent Mechanical Properties
Dong-Mei Li1 , Lan-Sheng Chen1 , Peng Yu1* , Ding Ding2 , and Lei Xia2
1 Chongqing Key Laboratory of Photo-Electric Functional Materials, College of Physics and Electronic Engineering, Chongqing Normal University, Chongqing 401331, China2 Laboratory for Microstructure & Institute of Materials, Shanghai University, Shanghai 200072, China
Abstract :A new Cu-based bulk metallic glass composite of nominal composition (at.%) Cu$_{41}$Ni$_{27}$Ti$_{25}$Al$_{7}$ with excellent plasticity and a strong work-hardening behavior is fabricated. Strength above 1859 MPa and plasticity more than 11% are achieved under compression and tension modes. The deformation mechanism is proposed to the structural heterogeneities of the composite that promotes multiple shear bands meanwhile inhibits their free propagation, which results in the macroscopically plastic strain and work hardening. The alloy contains relatively cheap metals and has a low cost, which is beneficial to industrial applications.
收稿日期: 2020-06-01
出版日期: 2020-07-28
[1] Peker A and Johnson W L 1993 Appl. Phys. Lett. 63 2342
[2] Wang W H 2012 Prog. Mater. Sci. 57 487
[3] Greer A L 2011 Nat. Mater. 10 88
[4] Ding S, Liu Y, Li Y, Liu Z, Sohn S, Walker F J and Schroers J 2014 Nat. Mater. 13 494
[5] Chen M W 2008 Annu. Rev. Mater. Res. 38 445
[6] Şopu D, Scudino S, Bian X L, Gammer C and Eckert J 2020 Scr. Mater. 178 57
[7] Chen G, Cheng J L and Liu C T 2012 Intermetallics 28 25
[8] Xiong J, Liu Y, Yu A, Liu B, Yu K, Huang X and Yang X J 2018 J. Alloys Compd. 741 1212
[9] González S, Louzguine-Luzgin D V, Perepezko J H and Inoue A 2010 Intermetallics 18 859
[10] Hays C C, Kim C P and Johnson W L 2000 Phys. Rev. Lett. 84 2901
[11] Qiao J W, Jia H L and Liaw P K 2016 Mater. Sci. & Eng. R 100 1
[12] Hofmann D C, Suh J Y, Wiest A, Duan G, Lind M L, Demetriou M D and Johnson W L 2008 Nature 451 1085
[13] Byrne C J and Eldrup M 2008 Science 321 502
[14] Launey M E, Hofmann D C, Suh J Y, Kozachkov H, Johnson W L and Ritchie R O 2009 Appl. Phys. Lett. 94 241910
[15] Ding D, Zhang Y Q and Xia L 2015 Chin. Phys. Lett. 32 106101
[16] Pauly S, Das J, Bednarcik J, Mattern N, Kim K B, Kim D H and Eckert J 2009 Scr. Mater. 60 431
[17] Hofmann D C 2010 Science 329 1294
[18] Pauly S, Liu G, Wang G, Kühn U, Mattern N and Eckert J 2009 Acta Mater. 57 5445
[19] Zong H T, Ma M Z, Zhang X Y, Qi L, Li G, Jing Q and Liu R P 2011 Chin. Phys. Lett. 28 036103
[20] Chu C L, Chung C Y, Lin P H and Wang S D 2004 Mater. Sci. & Eng. A 366 114
[21] Szuecs F, Kim C P and Johnson W L 2001 Acta Mater. 49 1507
[22] He G, Eckert J, Löser W and Schultz L 2003 Nat. Mater. 2 33
[23] Han J H, Kim K B, Yi S, Park J M, Sohn S W, Kim T E and Eckert J 2008 Appl. Phys. Lett. 93 141901
[24] Abdeljawad F, Fontus M and Haataja M 2011 Appl. Phys. Lett. 98 031909
[25] Abdeljawad F and Haataja M 2010 Phys. Rev. Lett. 105 125503
[26] Wu Y, Ma D, Li Q K, Stoica A D, Song W L, Wang H and Wang X L 2017 Acta Mater. 124 478
[1]
. [J]. 中国物理快报, 2022, 39(11): 119902-.
[2]
. [J]. 中国物理快报, 2022, 39(4): 46401-046401.
[3]
. [J]. 中国物理快报, 2022, 39(3): 36401-.
[4]
. [J]. 中国物理快报, 2017, 34(2): 26402-026402.
[5]
. [J]. 中国物理快报, 2016, 33(04): 46401-046401.
[6]
. [J]. 中国物理快报, 2014, 31(11): 116102-116102.
[7]
. [J]. 中国物理快报, 2014, 31(10): 106401-106401.
[8]
KE Hai-Bo,ZHAO Zuo-Feng,WEN Ping**,WANG Wei-Hua. Specific Heat in a Typical Metallic Glass Former [J]. 中国物理快报, 2012, 29(4): 46402-046402.
[9]
ZHANG Chun-Zhi;HU Li-Na**;BIAN Xiu-Fang;YUE Yuan-Zheng;
. Fragile-to-Strong Transition in Al-Ni-M (M=La, Pr, Nd) Metallic Glasses [J]. 中国物理快报, 2010, 27(11): 116401-116401.
[10]
ZHUO Long-Chao;PANG Shu-Jie;WANG Hui;ZHANG Tao. Ductile Bulk Aluminum-Based Alloy with Good Glass-Forming Ability and High Strength [J]. 中国物理快报, 2009, 26(6): 66402-066402.
[11]
JIANG Min-Qiang;JIANG Si-Yue$;DAI Lan-Hong;. Inherent Shear-Dilatation Coexistence in Metallic Glass [J]. 中国物理快报, 2009, 26(1): 16103-016103.
[12]
YANG Hong-Wang;TONG Wei-Ping;ZHAO Xiang;ZUO Liang;WANG Jian-Qiang. Observation of β-Relaxation in Sub-Tg Isothermally Annealed Al-Based Metallic Glasses [J]. 中国物理快报, 2008, 25(9): 3357-3359.
[13]
GUO Xiao-Lin;SHAN De-Bin;MA Ming-Zhen;GUO Bin. Compressive Deformation Induced Nanocrystallization of a Supercooled Zr-Based Bulk Metallic Glass [J]. 中国物理快报, 2008, 25(6): 2173-2176.