Silver-Doping Induced Lattice Distortion in TiO2 Nanoparticles
WU Xue-Wei1,2, WU Da-Jian1, LIU Xiao-Jun1
1Department of Electronic Science and Engineering, Key Lab of Modern Acoustics of MOE, Nanjing University, Nanjing 2100932State Key Laboratory of Electrical Insulation and Power Equipment, Xi'an Jiaotong University, Xi'an 710049
Silver-Doping Induced Lattice Distortion in TiO2 Nanoparticles
WU Xue-Wei1,2, WU Da-Jian1, LIU Xiao-Jun1
1Department of Electronic Science and Engineering, Key Lab of Modern Acoustics of MOE, Nanjing University, Nanjing 2100932State Key Laboratory of Electrical Insulation and Power Equipment, Xi'an Jiaotong University, Xi'an 710049
摘要The Ag-doping effects on TiO2 nanoparticles are investigated by means of x-ray diffraction (XRD) and Raman scattering spectroscopy. XRD and Raman results indicate that Ag-doping stabilizes the rutile phase in TiO2. We find an Ag-doping induced lattice expansion in both anatase and rutile phases. The Ag-doping has different influences on the lattice distortion for anatase and rutile phases, that is, the c/a-value for the anatase phase decreases with 0.5% Ag-doping and then increases with 1% Ag-doping while that for the rutile phase shows a gradual increase with increasing Ag-doping. We have ascribed the different variations of lattice distortion due to Ag-doping to the change of interfacial interaction between the anatase and rutile phases induced by different Ag concentrations.
Abstract:The Ag-doping effects on TiO2 nanoparticles are investigated by means of x-ray diffraction (XRD) and Raman scattering spectroscopy. XRD and Raman results indicate that Ag-doping stabilizes the rutile phase in TiO2. We find an Ag-doping induced lattice expansion in both anatase and rutile phases. The Ag-doping has different influences on the lattice distortion for anatase and rutile phases, that is, the c/a-value for the anatase phase decreases with 0.5% Ag-doping and then increases with 1% Ag-doping while that for the rutile phase shows a gradual increase with increasing Ag-doping. We have ascribed the different variations of lattice distortion due to Ag-doping to the change of interfacial interaction between the anatase and rutile phases induced by different Ag concentrations.
[1] Fujishima A and Honda K 1972 Nature 238 5551 [2] Andersson M, \"{Osterlund L, Ljungstr\"{om S andPalmqvist A 2002 J. Phys. Chem. B 106 10674 [3] Weissmann M and Errico L A 2007 Physica B 398179 [4] Djerdj I and Tonejc A M 2006 J. Alloys Compd. 413 159 [5] Nuansing W, Ninmuang S, Jarernboon W, Maensiri S andSeraphin S 2006 Mater. Sci. Eng. B 131 147 [6] Samuel V, Pasricha R and Ravi V 2005 Ceram. Int. 31 555 [7] Ren L, Huang X T, Sun F L and He X 2007 Mater. Lett. 61 427 [8] Bacsa R, Kiwi J, Ohno T, Albers P and Nadtochenko V 2005 J. Phys. Chem. B 109 5994 [9] Asahi R, Morikawa T, Ohwaki T, Aoki K and Taga Y 2001 Science 293 269 [10] Colmenares J C, Aramend\'{\ia M A, Marinas A, Marinas JM and Urbano F J 2006 Appl. Catal. A 306 120 [11] Zhao G, Kozuka H and Yoko T 1996 Thin Solid Films 277 147 [12] Herrmann J M, Tahiri H, Ait-Ichou Y, Lassaletta G,Gonzalez-Elipe A R and Fernandez A 1997 Appl. Catal. B 13 219 [13] Xin B F, Ren Z Y, Hu H Y, Zhang X Y, Dong C L, Shi K Y,Jing L Q and Fu H G 2005 Appl. Surf. Sci. 252 2050 [14] Liu Y, Liu C Y, Zhang Z Y and Wang C Y 2001 Spectrochim. Acta A 57 35 [15] Zhou Y, Wang C Y, Liu H J, Zhu Y R, Chen Z Y 1999 Mater. Sci. Eng. B 67 95 [16] Park M S and Kang M 2008 Mater. Lett. 62 183 [17] Sena S, Mahanty S, Roy S, Heintz O, Bourgeois S andChaumont D 2005 Thin Solid Films 474 245 [18] Chang C C, Lin C K, Chan C C, Hsu C S and Chen C Y 2006 Thin Solid Films 494 274 [19] Xin B F, Jing L Q, Ren Z Y, Wang B Q and Fu H G 2005 J. Phys. Chem. B 109 2805 [20] Yu J G, Xiong J F, Cheng B and Liu S W 2005 Appl.Catal. B 60 211 [21] Cullity B D 1978 Elements of X-ray Diffraction(Massachustts: Addison-Wesley) p 102 [22] Ohno T et al 2004 Appl. Catal. A 265 115 [23] Li X H S, Fryxell G E, Wang C M and Engelhard M H 2008 Microporous Mesoporous Mater. 111 639 [24] Mo S D and Ching W Y 1995 Phys. Rev. B 5113023 [25] Orendorz A, Brodyanski A, L\"{osch J, Bai L H, Chen ZH, Le Y K, Ziegler C and Gnaser H 2007 Surf. Sci. 6014390