Anomalous Specific Heat Behavior of Nanocrystalline Fe at Low Temperatures
BAI Haiyang, LUO Jianlin, JIN Duo, SUN Jirong*
Cryogenic Laboratory, Chinese Academy of Sciences, Beijing 100080
* Institute of Physics, Chinese Academy of Sciences, Beijing 100080
Anomalous Specific Heat Behavior of Nanocrystalline Fe at Low Temperatures
BAI Haiyang;LUO Jianlin;JIN Duo;SUN Jirong*
Cryogenic Laboratory, Chinese Academy of Sciences, Beijing 100080
* Institute of Physics, Chinese Academy of Sciences, Beijing 100080
关键词 :
61.46.+w ,
65.40.-f
Abstract : The specific heat of nanocrystalline iron with grain size of 40nm has been measured in the low temperature range from 1.8 to 26K. The anomalous specific heat behavior of nanocrystalline iron is compared to that of the standard bulk iron. It is found that the electronic specific heat coefficient γ obtained at low temperatures decreases by about 50%. A T2 term in the heat capacity associated with surface modes has been clearly observed. A large enhancement of the specific heat at temperatures above 16K may be interpreted as the Einstein oscillator contributions.
Key words :
61.46.+w
65.40.-f
出版日期: 1995-09-01
引用本文:
BAI Haiyang;LUO Jianlin;JIN Duo;SUN Jirong*. Anomalous Specific Heat Behavior of Nanocrystalline Fe at Low Temperatures[J]. 中国物理快报, 1995, 12(9): 549-552.
BAI Haiyang, LUO Jianlin, JIN Duo, SUN Jirong*. Anomalous Specific Heat Behavior of Nanocrystalline Fe at Low Temperatures. Chin. Phys. Lett., 1995, 12(9): 549-552.
链接本文:
https://cpl.iphy.ac.cn/CN/
或
https://cpl.iphy.ac.cn/CN/Y1995/V12/I9/549
[1]
TONG Rui;WU Hui-Xia;QIU Xue-Qiong;QIAN Shi-Xiong;LIN Yang-Hui;CAI Rui-Fang. Optical Performance and Nonlinear Scattering of Soluble Polystyrene Grafted Multi-Walled Carbon Nanotubes [J]. 中国物理快报, 2006, 23(8): 2105-2108.
[2]
SONG Chen;XIA Yue-Yuan;ZHAO Ming-Wen;LIU Xiang-Dong;LI Ji-Ling;LI Li-Juan;LI Feng;HUANG Bo-Da. Ab Initio Calculation on Self-Assembled Base-Functionalized Single-Walled Carbon Nanotubes [J]. 中国物理快报, 2006, 23(8): 2210-2212.
[3]
WU Xu-Feng;XU Chun-Xiang;ZHU Guang-Ping;LING Yi-Ming. ZnO Nanorods Produced by the Method of Arc Discharge [J]. 中国物理快报, 2006, 23(8): 2165-2168.
[4]
WEI He-Lin;ZHANG Xi-Xiang;HUANG Han-Chen. Spontaneous Hillock Growth on Indium Film Surface [J]. 中国物理快报, 2006, 23(7): 1880-1883.
[5]
ZHANG Bing-Yun;LIANG Qi-Min;SONG Chen;XIA Yue-Yuan;ZHAO Ming-Wen;LIU Xiang-Dong;ZHANG Hong-Yu. Hydrogen Storage in Benzene Moiety Decorated Single-Walled Carbon Nanotubes [J]. 中国物理快报, 2006, 23(6): 1536-1549.
[6]
WEI He-Lin;HUANG Han-Chen;ZHANG Xi-Xiang. Growth of Indium Nanorods by Magnetron Sputtering [J]. 中国物理快报, 2006, 23(6): 1627-1630.
[7]
XIA Dong-Yan;DAI Lun;XU Wan-Jin;YOU Li-Ping;ZHANG Bo-Rui;RAN Guang-Zhao;QIN Guo-Gang;. Synthesis and PL Properties of ZnSe Nanowires with Zincblende and Wurtzite Structures [J]. 中国物理快报, 2006, 23(5): 1317-1320.
[8]
SHEN Min;WEI He-Lin;WANG Jian;LIU Zu-Li. Copper Nanobelt Reorientation by Molecular Dynamics Simulation [J]. 中国物理快报, 2006, 23(10): 2721-2724.
[9]
LI Ai-Yu; WANG Xiao-Chun; WEN Yu-Hua;ZHU Zi-Zhong. TiNi Monatomic Chains Stabilized by Alloying: a First-Principles Study [J]. 中国物理快报, 2006, 23(1): 182-185.
[10]
ZHANG Xi-Yan;WU Xiao-Lei;XIA Bao-Yu;ZHOU Ming-Zhe;ZHOU Shi-Jie;JIA Chong. Step Structure in Cold-Rolled Deformed Nanocrystalline Nickel [J]. 中国物理快报, 2005, 22(9): 2335-2337.
[11]
HU Xiao-Yong;GONG Qi-Huang;CHENG Bing-Ying;ZHANG Dao-Zhong. Abnormal Modulation of Dielectric Band Transmittance of Polystyrene Opal [J]. 中国物理快报, 2005, 22(8): 1930-1933.
[12]
ZHAO Pu-Qin;HU Dong-Sheng;WU Xing-Long. Quantum Confinement of Si Nanosphere with Radius Smaller than 1.2nm [J]. 中国物理快报, 2005, 22(6): 1492-1495.
[13]
WANG Bao-Lin;;ZHAO Ji-Jun;SHI Da-Ning;JIA Jian-Min;WANG Guang-Hou. Electronic and Elastic Properties of Helical Nickel Nanowires [J]. 中国物理快报, 2005, 22(5): 1195-1198.
[14]
CHAI Yang;YU Li-Gang;WANG Ming-Sheng;ZHANG Qi-Feng;WU Jin-Lei. Low-Field Emission from Iron Oxide-Filled Carbon Nanotube Arrays [J]. 中国物理快报, 2005, 22(4): 911-914.
[15]
LI Pei-Gang;FU Xiu-Li;CHEN Lei-Ming;ZHANG Hai-Ying;LI Ling-Hong;TANG Wei-Hua. Fabrication and Characterization of YBa2 Cu3 Oy Superconducting Nanowires [J]. 中国物理快报, 2005, 22(3): 651-653.