摘要Well-dispersed Fe3O4 nanoparticles are synthesized via an oxidization method with NaNO2 as oxidant. The microwave magnetic properties of the composites are studied with different volume fractions of Fe3O4 nanoparticles. It is found that a lower volume fraction corresponds to a higher magnetic resonance frequency. This could be ascribed to the enhancement of exchange interaction with a weakened dipolar interaction when the volume fraction decreases.
Abstract：Well-dispersed Fe3O4 nanoparticles are synthesized via an oxidization method with NaNO2 as oxidant. The microwave magnetic properties of the composites are studied with different volume fractions of Fe3O4 nanoparticles. It is found that a lower volume fraction corresponds to a higher magnetic resonance frequency. This could be ascribed to the enhancement of exchange interaction with a weakened dipolar interaction when the volume fraction decreases.
[1] Toneguzzo P, Viau G, Acher O, Fievet-Vincent F andFievet F 1998 Adv. Mater. 10 1032 [2] Che R C, Peng L M, Duan X F, Chen Q and Liang X L 2004 Adv. Mater. 16 401 [3] Wen F S, Yi H B, Qiao L, Zheng H, Zhou D, Li F S 2008 Appl. Phys. Lett. 92 042507 [4] Battle X and Labara A 2002 J. Phys. D 35 R15 [5] El-Hilo M, Chantrell R W, and Grady K O 1998 J. Appl.Phys. 84 5114 [6] Youssef J B and Brosseau C 2006 Phys. Rev. B 74 214413 [7] Stoner E C and Wohlfarth E P 1948 Philos. Trans. R.Soc. London 240 599 [8] Aharoni A 1996 Introduction to the Theory ofFerromagnetism (Oxford: Clarendon) chap 8 p 181 [9] Li H R 1990 Introduction to Physics of Dielectrics1st edn (Chengdu: University of Science and Technology of Chengdu) p167 (in Chinese) [10] Kittel C 1948 Phys. Rev. 73 155 [11] Chikazumi S 1997 Physics of Ferromagnetism 2nd edn(Oxford: Oxford University Press) pp 167 238 [12] Kell P E, Grad K O, Mayo P I and Chantrell R W 1989 IEEE Trans. Magn. 25 3881 [13] Blanco-Mantecon M and Grady K O 2006 J. Magn. Magn.Mater. 296 124 [14] Heydon G P, Hoon S R et al 1997 J. Phys. D: Appl.Phys. 30 1083 [15] Robinson A and Schwarzacher W 2003 J. Appl. Phys 93 7250 [16] Wohlfarth E P J 1958 Appl. Phys. Lett. 29 595 [17] Gao R W, Zhang D H, Li W et al 2000 J. Magn. Magn.Mater. 208 239 [18] Aharoni A 1991 J. Appl. Phys. 69 7762 [19] Wen F S, Yi H B, Qiao L, Zheng H, Zhou D and Li F S 2008 Appl. Phys. Lett. 92 042507
2009, Vol. 26 