Fluorescence Properties of Nd : CeF3 Crystals
GAO Ming, FENG Xiqi, HU Guanqin, YIN Zhiwen
Shanghai Institute of Ceramics, Academia Sinica, Shanghai 200050
Fluorescence Properties of Nd : CeF3 Crystals
GAO Ming;FENG Xiqi;HU Guanqin;YIN Zhiwen
Shanghai Institute of Ceramics, Academia Sinica, Shanghai 200050
关键词 :
78.20.Dj ,
78.45.+h
Abstract : Four Nd : CeF3 crystals doped with 0.1, 0.5, 1.0 and 2.0 wt.% Nd3+ are grown, their absorption and fluorescence spectra are measured. The absorption bands of Nd : CeF3 are much wider than that of Nd: YAG. The absorption peak at 353nm does not depend on Nd3+ concentration linearly and there exists no concentration quenching effect while Nd3+ concentration is less than 2.0wt.%. The fluorescence lifetime and the effective stimulated cross section are measured, respectively, as Tr = 300μs and σc = 2.4 x 10-20 cm2 .
Key words :
78.20.Dj
78.45.+h
出版日期: 1994-07-01
[1]
ZHANG Qin-Yuan;YANG Gang-Feng;S. Buddhudu;JIANG Zhong-Hong;. UV-Blue Upconverted Emission from Nd3+ -Doped InF3 -Based Heavy-Metal Fluoride Glasses for Blue Upconversion Fibre Laser [J]. 中国物理快报, 2005, 22(3): 715-718.
[2]
LI Tao;ZHANG Qin-Yuan;LIU Yue-Hui;ZHANG Jun-Jie;DENG Zai-De;JIANG Zhong-Hong;. Infrared-to-Visible Upconversion and 1.53-μm Emission of Er3+ -Doped Al(PO3 )3 -Based Fluorophosphate Glass [J]. 中国物理快报, 2004, 21(6): 1147-1149.
[3]
HE Yong-Jun;HUANG Zhen-Li;WANG He-Zhou. Mechanism of Low Threshold Lasing of Dye Solution Embedding in Nanoparticle Fractal Aggregates [J]. 中国物理快报, 2003, 20(2): 293-295.
[4]
XUE Ling-Ling;ZHANG Chun-Ping;WANG Xin-Yu;ZHU Ming-Yao;ZHANG Lian-Shun;CHI Rong-Hua;ZHANG Jian-Dong;ZHANG Guang-Yin
. Monte Carlo Simulation of Light Transport in Five-Layered Skin Tissue [J]. 中国物理快报, 2000, 17(12): 909-911.
[5]
LI Hui;LU Zu-kang;LIN Lei;XIE Shu-sen. Light Scattering Properties of Biotissue Versus Equivalent Particle Size Distribution [J]. 中国物理快报, 1999, 16(4): 290-292.
[6]
GUO Chang-xin;FU Zhu-xi;SHI Chao-shu. Ultraviolet Super-Radiation Luminescence of Sputtering ZnO Film Under Cathode-Ray Excitation at Room Temperature [J]. 中国物理快报, 1999, 16(2): 146-148.
[7]
LIU Xian-cai;HU Guan-qin;FENG Xi-qi;LI Pei-jun;ZHANG Ming-rong;XU Li;YIN Zhi-wen. Influence of Sb on the Scintillation Properties of Lead Tungstate Crystal [J]. 中国物理快报, 1999, 16(10): 761-763.
[8]
ZHANG Guo-quan;ZHANG Guang-yin;LIU Si-min;XU Jing-jun;SUN Qian;LIU Jian-jun. Valence and Electronic Shell Configuration Characters of Damage-Resistant Dopants in LiNbO3 Crystals [J]. 中国物理快报, 1998, 15(9): 686-688.
[9]
LEI Ning;FENG Xi-qi;HU Guan-qin;YIN Zhi-wen;YUAN Shuai;XUE Shan-hua;HOU Xiao-yuan. Energy Transfer in Er:CeF3 Crystals [J]. 中国物理快报, 1998, 15(8): 603-604.
[10]
YANG Bao;MING Hai;ZHANG Qi-jin;XIE Jian-ping. Characterization of Clusters in a Novel Nd3+ -Doped Polymer Optical Fiber [J]. 中国物理快报, 1998, 15(4): 272-274.
[11]
KONG Yong-fa;WEN Jin-ke;YANG Zheng-fang. Photorefraction Resistance of Na2 O-Doped Lithium Niobate Single Crystals [J]. 中国物理快报, 1997, 14(8): 629-632.
[12]
LI Yi;SU Xiyu;SONG Lianke;ZHANG Binglin;MENG Xiangsheng. Scattering Window Material: Transparent A12 O3 Ceramics and Its Fabrication [J]. 中国物理快报, 1995, 12(7): 393-395.
[13]
XIE Fali;WU Baichang;MAO Hongwei;CHEN Chuangtian. Efficient Generation of Deep Ultraviolet Radiation Using LiB3 O5 Crystal [J]. 中国物理快报, 1992, 9(5): 240-242.
[14]
SHI Hongtao;ZHENG Youdou;WAND Yongbin;YUAN Renkuan. Current-Induced Light Emission from a Laterally Anodizing Porous Silicon Device [J]. 中国物理快报, 1992, 9(10): 555-557.
[15]
LIN Shujie;CHEN Chuangtian. CALCULATION OF THE SECOND-ORDER OPTICAL SUSCEPTIBILITIES OF SOME BENZENE DERIVATIVE MOLECULES AND CRYSTALS
[J]. 中国物理快报, 1990, 7(6): 268-271.