Tailoring the Microstructure of NiZn Ferrite for Power Field Applications

State Key Laboratory of Electronic Thin Films and Integrated Devices, University of Electronic Science and Technology of China, Chengdu 610054

Received Date: May 01, 2012

Published Date: July 31, 2012

Abstract

The effects of grain size and magnetic domain state on the power loss (from low to high induction conditions) and permeability characteristics of NiZn ferrites are investigated. It is found that under relatively low induction conditions (B_m<50 mT), a NiZn ferrite with a dense and monodomain microstructure obtains the lowest power loss. However, a NiZn ferrite with a larger average grain size displays a lower power loss under high induction conditions, and the influence of domain state on power loss is inconspicuous. Extremely large grain size and closed pores also lead to a poor frequency stability of permeability. Thus, synthetically considering the power loss and permeability characteristics, a NiZn ferrite with an even and large average grain size also has few closed pores and is the best choice for use under high induction conditions.

FullText(HTML)

[1]	Lucas A, Lebourgeois R, Mazaleyrat F and Laboure E 2010 Appl. Phys. Lett. 97 182502 doi: 10.1063/1.3507266
[2]	Su H, Zhang H W, Tang X L, Jing Y L and Liu Y L 2007 J. Magn. Magn. Mater. 310 17
[3]	Mirzaee O, Shafyei A, Golozar M A and Shokrollahi H 2008 J. Alloys. Compd. 461 312
[4]	Nabiyouni G, Jafari Fesharaki M, Mozafari M and Amighian J 2010 Chin. Phys. Lett. 27 126401
[5]	Zhou X, Hou Z L, Li F and Qi X 2010 Chin. Phys. Lett. 27 117501
[6]	Matsuo Y, Inagki M, Tomozawa T and Nakao F 2001 IEEE Trans. Magn. 37 2359
[7]	Sun K, Lan Z W, Yu Z, Li L Z, Huang J M and Zhao X N 2008 J. Phys. D 41 235002
[8]	Su H, Zhang H W, Tang X L and Jing Y L 2008 J. Appl. Phys. 103 093903
[9]	CheolGi K, Rao B P and Chong-Oh K 2007 Mater. Lett. 61 1601
[10]	Van D Z P J, Van D V P J and Rekveldt M T 1996 Appl. Phys. Lett. 69 2927
[11]	Van D Z P J, Kolenbrander M and Rekveldt M T 1998 J. Appl. Phys 83 6870
[12]	Hachiya M, Iijima Y, Sato N, Kawano K, Mizuno Y and Kishi H 2008 10^th International Conference on Ferrites p 224
[13]	Han Z Q 2008 J. Magn. Mater. Devices 39 7 (in Chinese)
[14]	Kondo K, Chiba T and Yamada S 2003 J. Magn. Magn. Mater. 254-255 541
[15]	Kondo K, Chiba T, Yamada S and Otsuki E 2000 J. Appl. Phys. 87 6229
[16]	Su H, Zhang H W, Tang X L and Shi Y 2008 J. Magn. Magn. Mater. 320 483
[17]	Hanuszkiewicz J, Holz D, Eleftheriou E, Zaspalis V 2008 J. Appl. Phys. 103 103907

Article views (1) PDF downloads (558)

Turn off MathJax

Article Contents

Abstract

Article Text

References

Export File