Abstract
We present a study of thermal stability of the top spin valve with a structure of seed Ta (5nm)/Co75Fe25 (5nm)/Cu (2.5nm)/Co75Fe25 (5nm)/Ir20Mn80 (12nm)/cap Ta (8nm) deposited at room temperature by magnetron sputtering. A vibrating sample magnetometer fixed with a heater was used to record the magnetic hysteresis loops at variational temperatures and x-ray diffraction was performed to characterize the structure of the multilayer. The exchange field Hex and the coercivity of the pinned CoFe layer Hcp decrease monotonically with increasing temperature. The coercivity of the free CoFe layer Hcf in the spin valve shows a maximum at 498K. The temperature dependences of Hex, Hcp and Hcf have also been discussed. -
References
[1] Tanoue S, Tabuchi K and Sawasaki T 2001 J. Magn.Magn. Mater. 233 164 [2] Nishioka K 1999 J. Appl. Phys. 86 6305 [3] Khapikov A F, Harrell J W, Fujiwara H and Hou C 2000 J. Appl. Phys. 87 4954 [4] Driel J , Boer F R , Lenssen K M H and Coehoorn R 2000 J. Appl. Phys. 88 975 [5] Choo D, Chantrell R W, Lamberton R, Johnston A and O'GradyK 2007 J. Appl. Phys. 101 09E521 [6] Fulcomer E and Charap S H 1972 J. Appl. Phys. 43 4190 [7] Lee D R, Freeland J W, Choi Y, Srajer G., Metlushko V andIlic B 2007 Phys. Rev. B 76 144425 [8] Hayakawa J, Takahashi H, Ito K, Fujimori M, Heike S,Hashizume T, Ichimura M, Ikeda S and Ohno H 2005 J. Appl.Phys. 97 114321 [9] Telling N D, Jones G A, Georgieva M T and Grundy P J2004 J. Magn. Magn. Mater. 272 1274 [10] Lim C K, Chapman J N, Rahman M, Johnston A B andO'Donnell D O 2002 J. Phys. D: Appl. Phys. 35 2344 [11] Kaka S, Pufall M R, Rippard W H, Silva T J, Russek S E,Katine J A and Carey M 2005 J. Magn. Magn. Mater. 286375 [12] Grollier J, Boulenc P, Cros V, Hamzic A, Vaures A andFert A 2004 J. Appl. Phys. 95 6777 [13] Morecroft D, Aken B B, Prieto J L, Kang D J, Burnell Gand Blamire M G 2005 J. Appl. Phys. 97 054302 [14] Jo S and Seigler M A 2007 J. Magn. Magn. Mater. 316 93 [15] Yoon S Y, Lee D H, Jeong K H, Yoon D H and Suh S J 2004 Mater. Sci. Forum 449 1065 [16] Yoon S Y, Lee D H, Jeon D M, Kim J H, Yoon D H and Suh SJ 2004 J. Magn. Magn. Mater. 272 1879 [17] Anderson G W, Pakala M and Huai Y M 2000 IEEE Trans.Magn. 362 605 [18] Lamy Y, Viala Band Prejbeanu I L 2005 IEEE Trans.Magn. 41 3517 [19] Zeltser A M and Pentek K 1998 IEEE Trans. Magn. 34 1417 [20] Chen Y T, Jen S U, Yao Y D, Wu J M, Hwang G H, Tsai T L,Chang Y C and Sun A C 2006 J. Magn. Magn. Mater. 304 e71 [21] Stamps R L 2000 J. Phys. D: Appl. Phys. 33R247 [22] Malozemoff A P 1988 J. Appl. Phys. 63 3874 [23] Rickart M, Guedes A, Franco N, Barradas N P, Diaz P,MacKenzie M, Chapman J N and Freitas P P 2005 J. Phys. D: Appl.Phys. 38 2151 [24] Yang T and Lai W Y 1999 J. Phys. D: Appl. Phys. 32 2856 [25] Stobiecki T, Kanak J, Wrona J, Reiss G and Bruckl H 2007 J. Magn. Magn. Mater. 316 e998 [26] Massalski T B, Okamoto H, Subramanian P R and Kacprzak L1990 Binary alloy Phase Diagrams (Cleveland, OH: American Societyfor Metals) vol 1 [27] Pakala M, Huai Y and Anderson G 2000 IEEE Trans.Magn. 36 2620 [28] Enders A, Peterka D, Repetto D, Lin N, mitrievA D andKern K 2003 Phys. Rev. Lett. 90 217203
Impact Factor 2023: 3.5 | CiteScore 2023: 5.9 | Time to First Decision: 28 days
DownLoad: