Magnetic Properties of Ni-Zn Ferrite Prepared with the Layered Precursor Method |
| ZHOU Xin1, HOU Zhi-Ling1, LI Feng2, QI Xin**
|
1Department of Physics and Electronics, Beijing University of Chemical Technology, Beijing 100029
2State Key Laboratory of Chemical Resource Engineering, Beijing University of Chemical Technology, Beijing 100029
|
|
| Cite this article: |
|
ZHOU Xin, HOU Zhi-Ling, LI Feng et al 2010 Chin. Phys. Lett. 27 117501 |
|
|
|
|
Abstract We prepare NiZnFe2O4 soft magnetic ferrites with different molar ratios with the layered precursor method and investigate their magnetic properties. In the layered precursor, metal ions are scattered on the layer plate in a certain way on account of the effect of lowest lattice energy and lattice orientation. After high temperature calcinations, spinel ferrites with uniform structural component and single magnetic domain can be obtained, and the magnetic property is improved greatly. NiZnFe2O4 ferrites prepared have the best specific saturation magnetization of 79.15 emu⋅g−1, higher than that of 68 emu⋅g−1 prepared by the chemical co-precipitation method and that of 59 emu⋅g−1prepared by the emulsion-gel method. Meanwhile the coercivity of NiZnFe2O4 ferrites prepared by layered precursor method is 14 kA⋅m−1, lower than that of 50 emu⋅g−1 prepared by the co-precipitation method and that of 59 emu⋅g−1 prepared by the emulsion-gel method.
|
| Keywords:
75.50.Dd
75.50.Gg
|
|
|
Received: 21 August 2010
Published: 22 October 2010
|
|
|
|
|
|
|
|
[1] Titulaer M K, Jansen J B H and Geus J W 1994 Clays Clay Miner. 42 249
[2] Cao M S, Liu H T, Chen Y J, Wang B and Zhu J 2003 Sci. Chin. E 46 104
[3] Cao M S, Wang R G, Fang X Y, Cui Z X, Chang T J and Yang H J 2001 Powder Technol. 115 96
[4] Wang J M, Wang Y F, Jiang C B and Xu H B 2006 Chin. Phys. Lett. 23 1293
[5] Vucclic M, Jones W and Moggride G D 1997 Clays Clay Miner. 45 803
[6] Sugimoto M 1999 J. Am. Ceram. Soc. 82 269
[7] Mohapatra M, Brajesh P, Chandan V, Anand S, Das R P and Verma H C 2005 J. Magn. Mater 295 46
[8] Li F, Liu X F, Yang Q Z, Liu J J, David G E and Duan X 2005 Mater. Res. Bull. 40 1246
[9] Wu Z, Wang X and Wang F 2007 Chin. Phys. Lett. 24 3249
[10] Busetto C, Del Piero G, Mamara G, Friiro F and Vaccar A 1984 J. Catal. 85 260
[11] Zhou X D, Qi X and Li F 2009 Mater. Mech. Engin. 33 88 (in Chinese)
[12] Castro S and Gayoso M 1997 J. Solid State Chem. 134 227
[13] Mydeen K, Yu Y and Jin C 2008 Chin. Phys. Lett. 25 3177
[14] Constantion V R L and Pinnavaia T J 1998 Inorg. Chem. 34 2086
[15] Taylor R M 1980 Clay Miner. 15 369
[16] Nathani H, Gubbala S and Misra R D K 2005 Mater. Sci. Engin. B 121 128
[17] \v{S}epelak V, Baabe D, Litterst F J and K D Becker 2000 J. Appl. Phys. 88 5884
[18] Costa A C F M, Tortella E, Morelli M R and Kiminami R H G A 2003 J. Magn. Magn. Mater. 256 174
[19] Trifirband F, Vaccari A, Atwood J L, Lehn J M, Davies J E D, MacNicol D D and Vogtle F 1996 Comprehensive Supramolecular Chemistry (Oxford: Pergamon) vol 7 chap 10
[20] Pilai V 1992 IEEE Trans. Magn. Mater. 116 299
[21] Kahn M L and Zhang Z J 2001 Appl. Phys. Lett. 78 3651
[22] Zhang H W, Shi Y and Zhong Z Y 2002 Chin. Phys. Lett. 19 269
[23] Bellotto M, Rebours B, Clause O, Lynch J, Bazin D and Elkaim E 1996 J. Phys. Chem. 100 8535
[24] Fernandez J M, Ulibarri M A and Labajos F M, Rives V 1998 J. Mater. Chem. 8 2507
[25] Liu Y, Zhang J, Ren Z and Cao S 2007 Chin. Phys. Lett. 24 210
[26] Heneda K et al 1987 IEEE Trans. Magn. Mater. 23 3134
[27] Huang Y Q, Hou Z L, Song W L, Yuan J and Cao M S 2009 Chin. Phys. Lett. 26 057701
[28] Kang Y Q, Cao M S, Shi X L and Hou Z L 2007 Surf. Coatings Technol. 201 7201
[29] Liu H T, Cao M S, Qiu C J and Zhu J 2003 Mater. Sci. Forum 423 427 |
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|