Structure and Raman Spectroscopy of Nanocrystalline TiO2 Powder Derived by Sol-Gel Process |
ZHOU Qi-fa;WU Shang-hua;ZHANG Qing-qi;ZHANG Jin-xiu;CHEN Jian1;ZHANG Wei-hong1 |
Department of Physics, Zhongshan University, Guangzhou 510275
Instrument Analysis and Research Center, Zhongshan University, Guangzhou 510275 |
|
Cite this article: |
ZHOU Qi-fa, WU Shang-hua, ZHANG Qing-qi et al 1997 Chin. Phys. Lett. 14 306-309 |
|
|
Abstract Nanocrystalline TiO2 powder was prepared by sol-gel process. The structures of the as-prepared and the TiO2 powder heat-treated at different temperatures were studied by thermogravimetric analyzer, differential thermal analysis, x-ray diffraction, and Raman spectra. As the powder was heat-treated at 350°C, it turned into tetragonal anatase structure. A structural transformation from anatase to rutile type occurred and the grains of the powder grew drastically when the powder was heat-treated at above 550°C. The structural transformation from anatase to rutile type completed at 750°C. The Raman spectra of TiO2 nanocrystalline powder were also studied.
|
Keywords:
78.66.Sq
42.65.An
42.70.Nq
|
|
Published: 01 April 1997
|
|
PACS: |
78.66.Sq
|
(Composite materials)
|
|
42.65.An
|
(Optical susceptibility, hyperpolarizability)
|
|
42.70.Nq
|
(Other nonlinear optical materials; photorefractive and semiconductor materials)
|
|
|
|
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|