Ferromagnetism from Co-Doped ZnO Nanocantilevers above Room Temperature |
ZHOU Shao-Min, WANG Peng, LI Sheng, ZHANG Bin, GONG He-Chun, DU Zu-Liang |
Key Lab for Special Functional Materials of Ministry of Education, Henan University, Kaifeng 475004 |
|
Cite this article: |
ZHOU Shao-Min, WANG Peng, LI Sheng et al 2008 Chin. Phys. Lett. 25 4446-4448 |
|
|
Abstract At low temperature (400°C), chemical vapour deposition (CVD) is employed to make comb-like Co-doped ZnO nanocantilever arrays (NAs). The magnetization curves of the as-synthesized Co-doped ZnO NAs indicate the existence of above-room-temperature ferromagnetism (ARTFM) (Curie temperature, Tc>300K) whereas undoped ZnO NAs does not. The corresponding ferromagnetic source mechanism is discussed, in which defects play an important role due to the strong green light emission.
|
Keywords:
81.05.Dz
81.16.Rf
75.75.+a
75.50.Pp
|
|
Received: 15 June 2008
Published: 27 November 2008
|
|
|
|
|
|
[1] Wang Z L et al 2003 Phys. Rev. Lett. 91 185502 [2] Zhou S M et al 2003 Micron 36 55 [3] Zhang B et al 2003 Phys. Lett. A 372 2300 [4] Dietl T et al 2000 Science 287 1019 [5] Matsumoto Y et al 2000 Science 291 854 [6] Ueda K et al 2001 Appl. Phys. Lett. 79 988 [7] Thurn-Albrecht T et al 2000 Science 290 2126 [8] Whitney T et al 1993 Science 261 1316 [9] Jian W B et al 2006 Phys. Rev. B 73 233308 [10] Khare N et al 2006 Adv. Mater. 18 1449 [11] Zhou S M 2007 Mater. Lett. 61 119 [12] Zhang B et al 2008 Chin. Sci Bull. 53 390 [13] Schwartz D et al 2004 Appl. Phys. Lett. 851395 [14] Cui Jet al 2006 Phys. Rev. B 74 045416 [15] Yan H et al 2007 Appl. Phys. Lett. 90 082503 [16] Cui J et al 2007 Appl. Phys. Lett. 87 133108 [17] Schwartz D et al 2007 J. Am. Chem. Soc. 12513205 [18] Naeem M et al 2007 J. Phys.: Condens. Matter 20 025210 |
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|