Blue Upconversion Emission in Yb3+ and Tm3+ Codoped Lead-Germanate-Tellurite Glasses |
YANG Zhong-Min;XU Shi-Qing;WEN Lei;JIANG Zhong-Hong |
Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Sciences, Shanghai 201800 |
|
Cite this article: |
YANG Zhong-Min, XU Shi-Qing, WEN Lei et al 2004 Chin. Phys. Lett. 21 1124-1127 |
|
|
Abstract Intense blue and red upconversion emissions have been observed in Yb3+/Tm3+ co-doped 0.05 K2O-0.1ZnO-0.1BaO-0.2PbO-0.2GeO2-0.35TeO2 glasses under the pump of 976-nm laser diode. The dependence of the intensity of the upconversion emissions on the Tm3+ concentration has been studied in order to determine the ion concentration and the involved mechanism. The blue emission centred at 476 nm decreases and the 792-nm red emission increases with the increasing Tm3+ concentration. Subsequently, the dependence of upconversion emission intensity on the excitation power is investigated. It is found that the intensity ratio between the 792-nm red and 476-nm blue emissions decreases with the increasing pump energy.
|
Keywords:
71.35.Fy
78.20.-e
73.61.Jc
|
|
Published: 01 June 2004
|
|
PACS: |
71.35.Fy
|
|
|
78.20.-e
|
(Optical properties of bulk materials and thin films)
|
|
73.61.Jc
|
(Amorphous semiconductors; glasses)
|
|
|
|
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|