Thermoelectric Properties of Te-Doped Ba0.32Co4Sb12−xTexPrepared at HPHT | ||
REN Guo-Zhong1, LIU Yang1, MA Hong-An2, SU Tai-Chao2, LIN Le-Jing1, DENG Le2, JIANG Yi-Ping2, ZHENG Shi-Zhao2, JIA Xiao-Peng2** | ||
1Faculty of Materials, Optoelectronics and Physics, Xiangtan University, Xiangtan 411105 2National Lab of Superhard Materials, Jinlin University, Changchun 130012 |
||
收稿日期 2010-04-23 修回日期 1900-01-01 | ||
Supporting info | ||
[1] DiSalvo F J 1999 Science 285 703 [2] Mi J L, Zhao X B, Zhu T J et al 2008 J. Alloys Compd. 452 225 [3] Liu K G, Zhang J X and Xiang D 2007 J. Mater. Proc. Technol. 184 257 [4] Wu H Q, Xu D M, Wang Q, Wang Q Y et al 2008 J. Alloys Compd. 463 78 [5] Stoch A, Guzdek P, Stoch P, Pszczola et al 2009 J. Alloys Compd. 467 83 [6] Nordstrom L and Singh D J 1996 Phys. Rev . B 53 1103 [7] Caillat T, Borshchevsky A and Fleurial J P 1996 J. Appl. Phys. 80 4442 [8] Zhou Z, Uher C, Jewell A and Caillat T 2005 Phys. Rev. B 71 235209 [9] Morelli D T and Meisner G P 1995 J. Appl. Phys. 77 3777 [10] Pei Y Z, Chen L D, Zhang W, Shi X et al 2006 Appl. Phys. Lett. 89 221107 [11] Tang X, Zhang Q, Chen L and Goto T 2005 J. Appl. Phys. 97 093712 [12] Stiewe C, Bertini L, Toprak M and Christensen M 2005 J. Appl. Phys. 97 044317 [13] Chen L D, Kawahara T, Tang X F and Goto T 2001 J. Appl. Phys. 90 1864 [14] Qin B K, Li X L, Li S S et al 2010 J. Inorg. Mater. 25 23 [15] Deng L, Ma H A, Su T C, Yu F R and Tian Y J 2009 Mater. Lett. 63 2139 [16] Peng J Y, Yang J, Zhang T J, Song X L and Chen Y H 2004 J. Alloys Compd. 381 313 [17] Zhang X, Lu Q M, Zhang J X, Wei Q et al 2007 J. Alloys Compd. 457 368 [18] Yang L, Hng H, Cheng H, Sun T, Ma J et al 2008 Mater. Lett. 62 2483 [19] Su T C, Jia X P, Ma H A, Zang C Y et al 2008 Mater. Lett. 62 3269 [20] Su T C, Jia X P, Ma H A, Jiang Y P et al 2009 J. Alloys Compd. 468 410 [21] Ma H A, Su T C, Zhu P W, Guo J G et al 2008 J. Alloys Compd. 454 415 [22] He Q Y, Hu S J, Tang X G, Lan Y C et al 2008 Appl. Phys. Lett. 93 042108 [23] Wojciechowski K T, Tobola J and Leszczyfiski 2003 J. Alloys Compd. 361 19 |
||